Rheological properties |
C | Melt volume-flow rate | 280 °C; 2.16 kg | cm³/(10 min) | ISO 1133-1 | 25 |
C | Molding shrinkage, parallel | 60x60x2; 280°C / WZ 110°C; 600 bar | % | ISO 294-4 | 0.2 |
C | Molding shrinkage, transverse | 60x60x2; 280°C / WZ 110°C; 600 bar | % | ISO 294-4 | 0.7 |
| Post- shrinkage, parallel | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.1 |
| Post- shrinkage, transverse | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.1 |
Mechanical properties (23 °C/50 % r. h.) |
C | Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 12000 |
C | Tensile Stress at break | 5 mm/min | MPa | ISO 527-1,-2 | 125 |
C | Tensile Strain at break | 5 mm/min | % | ISO 527-1,-2 | 1.6 |
C | Charpy notched impact strength | 23 °C | kJ/m² | ISO 179-1eA | <10 |
C | Charpy notched impact strength | -30 °C | kJ/m² | ISO 179-1eA | <10 |
| Izod impact strength | 23 °C | kJ/m² | ISO 180-1U | 35 |
| Izod notched impact strength | 23 °C | kJ/m² | ISO 180-1A | <10 |
| Izod notched impact strength | -30 °C | kJ/m² | ISO 180-1A | <10 |
| Flexural modulus | 2 mm/min | MPa | ISO 178-A | 11000 |
| Flexural strength | 2 mm/min | MPa | ISO 178-A | 175 |
| Flexural strain at flexural strength | 2 mm/min | % | ISO 178-A | 2.0 |
Thermal properties |
C | Melting temperature | 10 °C/min | °C | ISO 11357-1,-3 | 260 |
C | Temperature of deflection under load | 1.80 MPa | °C | ISO 75-1,-2 | 205 |
C | Temperature of deflection under load | 0.45 MPa | °C | ISO 75-1,-2 | 250 |
| Vicat softening temperature | 50 N; 120 °C/h | °C | ISO 306 | 220 |
C | Coefficient of linear thermal expansion, parallel | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.2 |
C | Coefficient of linear thermal expansion, transverse | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.5 |
| Glow wire test (GWFI) | 0.8 mm | °C | IEC 60695-2-12 | 750 |
| Glow wire test (GWFI) | 1.5 mm | °C | IEC 60695-2-12 | 750 |
| Glow wire test (GWFI) | 3.0 mm | °C | IEC 60695-2-12 | 750 |
| Glow wire test (GWIT) | 0.8 mm | °C | IEC 60695-2-13 | 775 |
| Glow wire test (GWIT) | 1.5 mm | °C | IEC 60695-2-13 | 775 |
| Glow wire test (GWIT) | 3.0 mm | °C | IEC 60695-2-13 | 775 |
Electrical properties (23 °C/50 % r. h.) |
C | Comparative tracking index CTI | Solution A | Rating | IEC 60112 | 225 |
Other properties (23 °C) |
C | Density | | kg/m³ | ISO 1183 | 1700 |
| Bulk density | | kg/m³ | ISO 60 | 900 |
Processing conditions for test specimens |
C | Injection molding-Melt temperature | | °C | ISO 294 | 280 |
C | Injection molding-Mold temperature | | °C | ISO 294 | 110 |
Processing recommendations |
| Drying temperature circulating air dryer | | °C | - | 120 |
| Drying time circulating air dryer | | h | - | 4-8 |
| Residual moisture content | | % | Acc. to Karl Fischer | 0.00-0.02 |
| Melt temperature (Tmin - Tmax) | | °C | - | 270-290 |
| Mold temperature | | °C | - | 100-130 |