Rheological properties |
| Molding shrinkage, parallel | 150x105x3; 300 °C / MT 80 °C; 400 bar | % | acc. ISO 294-4 | 0.23 | |
| Molding shrinkage, transverse | 150x105x3; 300 °C / MT 80 °C; 400 bar | % | acc. ISO 294-4 | 1.25 | |
| Post- shrinkage, parallel | 150x105x3; 120 °C; 4 h | % | acc. ISO 294-4 | 0.02 | |
| Post- shrinkage, transverse | 150x105x3; 120 °C; 4 h | % | acc. ISO 294-4 | 0.03 | |
Mechanical properties (23 °C/50 % r. h.) |
C | Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 15700 | 10700 |
C | Tensile Stress at break | 5 mm/min | MPa | ISO 527-1,-2 | 220 | 170 |
C | Tensile Strain at break | 5 mm/min | % | ISO 527-1,-2 | 2.5 | 4.0 |
C | Charpy impact strength | 23 °C | kJ/m² | ISO 179-1eU | 95 | 95 |
C | Charpy impact strength | -30 °C | kJ/m² | ISO 179-1eU | 100 | 100 |
C | Charpy notched impact strength | 23 °C | kJ/m² | ISO 179-1eA | 19 | 23 |
C | Charpy notched impact strength | -30 °C | kJ/m² | ISO 179-1eA | 15 | 15 |
| Izod notched impact strength | 23 °C | kJ/m² | ISO 180-1A | 14 | 18 |
| Izod notched impact strength | -30 °C | kJ/m² | ISO 180-1A | 11 | 11 |
| Flexural modulus | 2 mm/min | MPa | ISO 178-A | 14000 | 10300 |
| Flexural strength | 2 mm/min | MPa | ISO 178-A | 370 | 250 |
| Flexural strain at flexural strength | 2 mm/min | % | ISO 178-A | 3.0 | 5.0 |
| Flexural stress at 3.5 % strain | 2 mm/min | MPa | ISO 178-A | | 235 |
| Ball indentation hardness | | N/mm² | ISO 2039-1 | 290 | 160 |
Thermal properties |
C | Melting temperature | 10 °C/min | °C | ISO 11357-1,-3 | 263 | |
C | Temperature of deflection under load | 1.80 MPa | °C | ISO 75-1,-2 | ~250 | |
C | Temperature of deflection under load | 0.45 MPa | °C | ISO 75-1,-2 | ~250 | |
| Vicat softening temperature | 50 N; 120 °C/h | °C | ISO 306 | > 230 | |
Other properties (23 °C) |
C | Water absorption (Saturation value) | Water at 23 °C | % | ISO 62 | ~4 | |
C | Water absorption (Equilibrium value) | 23 °C; 50 % RH | % | ISO 62 | ~1.4 | |
C | Density | | kg/m³ | ISO 1183 | 1570 | |
| Bulk density | | kg/m³ | ISO 60 | ~700 | |
Processing conditions for test specimens |
C | Injection molding-Melt temperature | | °C | ISO 294 | 300 | |
C | Injection molding-Mold temperature | | °C | ISO 294 | 80 | |
Processing recommendations |
| Drying temperature dry air dryer | | °C | - | 80 | |
| Drying time dry air dryer | | h | - | 2-6 | |
| Residual moisture content | | % | Acc. to Karl Fischer | 0.03-0.12 | |
| Melt temperature (Tmin - Tmax) | | °C | - | 280-300 | |
| Mold temperature | | °C | - | 80-120 | |