Rheological properties |
C | Molding shrinkage, parallel | 60x60x2; 290 °C / MT 80 °C; 600 bar | % | ISO 294-4 | 0.44 | |
C | Molding shrinkage, transverse | 60x60x2; 290 °C / MT 80 °C; 600 bar | % | ISO 294-4 | 0.94 | |
| Post- shrinkage, parallel | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.06 | |
| Post- shrinkage, transverse | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.12 | |
Mechanical properties (23 °C/50 % r. h.) |
C | Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 9700 | 6100 |
C | Tensile Stress at break | 5 mm/min | MPa | ISO 527-1,-2 | 180 | 120 |
C | Tensile Strain at break | 5 mm/min | % | ISO 527-1,-2 | 3.5 | 8.0 |
C | Charpy impact strength | 23 °C | kJ/m² | ISO 179-1eU | 75 | 85 |
C | Charpy impact strength | -30 °C | kJ/m² | ISO 179-1eU | 65 | 75 |
C | Charpy notched impact strength | 23 °C | kJ/m² | ISO 179-1eA | 10 | 20 |
C | Charpy notched impact strength | -30 °C | kJ/m² | ISO 179-1eA | < 10 | < 10 |
| Charpy notched impact strength | -40 °C | kJ/m² | ISO 179-1eA | < 10 | < 10 |
| Izod impact strength | 23 °C | kJ/m² | ISO 180-1U | 70 | |
| Izod impact strength | -30 °C | kJ/m² | ISO 180-1U | 60 | |
| Izod notched impact strength | -30 °C | kJ/m² | ISO 180-1A | <10 | <10 |
| Izod notched impact strength | -40 °C | kJ/m² | ISO 180-1A | < 10 | < 10 |
| Flexural modulus | 2 mm/min | MPa | ISO 178-A | 9300 | 5700 |
| Flexural strength | 2 mm/min | MPa | ISO 178-A | 280 | 180 |
| Flexural strain at flexural strength | 2 mm/min | % | ISO 178-A | 4.0 | 6.5 |
| Flexural stress at 3.5 % strain | 2 mm/min | MPa | ISO 178-A | 265 | 150 |
C | Puncture maximum force | 23 °C | N | ISO 6603-2 | 896 | 1073 |
C | Puncture maximum force | -30 °C | N | ISO 6603-2 | 776 | |
C | Puncture energy | 23 °C | J | ISO 6603-2 | 3.1 | 4.7 |
C | Puncture energy | -30 °C | J | ISO 6603-2 | 1.9 | |
| Ball indentation hardness | | N/mm² | ISO 2039-1 | 205 | 105 |
Thermal properties |
C | Melting temperature | 10 °C/min | °C | ISO 11357-1,-3 | 262 | |
C | Temperature of deflection under load | 1.80 MPa | °C | ISO 75-1,-2 | 245 | |
C | Temperature of deflection under load | 0.45 MPa | °C | ISO 75-1,-2 | 250 | |
C | Temperature of deflection under load | 8.00 MPa | °C | ISO 75-1,-2 | 125 | |
| Vicat softening temperature | 50 N; 120 °C/h | °C | ISO 306 | 254 | |
C | Coefficient of linear thermal expansion, parallel | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.3 | |
C | Coefficient of linear thermal expansion, transverse | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.9 | |
C | Burning behavior UL 94 | 1.5 mm | Class | UL 94 | HB | |
C | Burning behavior UL 94 | 0.75 mm | Class | UL 94 | HB | |
C | Oxygen index | Method A | % | ISO 4589-2 | 26 | |
| Glow wire test (GWFI) | 2.0 mm | °C | IEC 60695-2-12 | 650 | |
| Burning behavior US-FMVSS302 | >=1.0 mm | | ISO 3795 | passed | |
C | Vicat softening temperature | 50 N; 50 °C/h | °C | ISO 306 | > 230 | |
Electrical properties (23 °C/50 % r. h.) |
C | Relative permittivity | 100 Hz | - | IEC 60250 | 4.0 | 12 |
C | Relative permittivity | 1 MHz | - | IEC 60250 | 3.6 | 4.5 |
C | Dissipation factor | 100 Hz | 10-4 | IEC 60250 | 80 | 3000 |
C | Dissipation factor | 1 MHz | 10-4 | IEC 60250 | 160 | 900 |
C | Volume resistivity | | Ohm·m | IEC 62631-3 | 1E13 | 1E09 |
C | Surface resistivity | | Ohm | IEC 62631-3 | 1E15 | 1E13 |
C | Electric strength | 1 mm | kV/mm | IEC 60243-1 | 35 | 30 |
C | Comparative tracking index CTI | Solution A | Rating | IEC 60112 | 450 | |
Other properties (23 °C) |
C | Water absorption (Saturation value) | Water at 23 °C | % | ISO 62 | 5.5 | |
C | Water absorption (Equilibrium value) | 23 °C; 50 % RH | % | ISO 62 | 2.0 | |
C | Density | | kg/m³ | ISO 1183 | 1360 | |
| Bulk density | | kg/m³ | ISO 60 | 700 | |
Processing conditions for test specimens |
C | Injection molding-Melt temperature | | °C | ISO 294 | 290 | |
C | Injection molding-Mold temperature | | °C | ISO 294 | 80 | |
Processing recommendations |
| Drying temperature dry air dryer | | °C | - | 80 | |
| Drying time dry air dryer | | h | - | 2-6 | |
| Residual moisture content | | % | Acc. to Karl Fischer | 0.03-0.12 | |
| Melt temperature (Tmin - Tmax) | | °C | - | 280-300 | |
| Mold temperature | | °C | - | 80-120 | |