Rheological properties |
C | Molding shrinkage, parallel | 60x60x2 | % | ISO 294-4 | 0.2 | |
C | Molding shrinkage, transverse | 60x60x2 | % | ISO 294-4 | 0.8 | |
| Post- shrinkage, parallel | 60x60x2 | % | ISO 294-4 | 0.1 | |
| Post- shrinkage, transverse | 60x60x2 | % | ISO 294-4 | 0.15 | |
Mechanical properties (23 °C/50 % r. h.) |
C | Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 11600 | 7700 |
C | Tensile Stress at break | 5 mm/min | MPa | ISO 527-1,-2 | 205 | 130 |
C | Tensile Strain at break | 5 mm/min | % | ISO 527-1,-2 | 3.2 | 5 |
C | Charpy impact strength | 23 °C | kJ/m² | ISO 179-1eU | 70 | 85 |
C | Charpy impact strength | -30 °C | kJ/m² | ISO 179-1eU | 60 | 55 |
C | Charpy notched impact strength | 23 °C | kJ/m² | ISO 179-1eA | 10 | 12 |
C | Charpy notched impact strength | -30 °C | kJ/m² | ISO 179-1eA | <10 | <10 |
| Izod impact strength | 23 °C | kJ/m² | ISO 180-1U | 65 | 80 |
| Izod impact strength | -30 °C | kJ/m² | ISO 180-1U | 60 | 55 |
| Izod notched impact strength | 23 °C | kJ/m² | ISO 180-1A | 10 | 13 |
| Izod notched impact strength | -30 °C | kJ/m² | ISO 180-1A | <10 | 13 |
| Flexural modulus | 2 mm/min | MPa | ISO 178-A | 11000 | 8000 |
| Flexural strength | 2 mm/min | MPa | ISO 178-A | 315 | 215 |
| Flexural strain at flexural strength | 2 mm/min | % | ISO 178-A | 3.7 | 6 |
| Flexural stress at 3.5 % strain | 2 mm/min | MPa | ISO 178-A | 310 | 185 |
C | Puncture maximum force | 23 °C | N | ISO 6603-2 | 760 | 1000 |
C | Puncture maximum force | -30 °C | N | ISO 6603-2 | 720 | 790 |
C | Puncture energy | 23 °C | J | ISO 6603-2 | 2.5 | 4 |
C | Puncture energy | -30 °C | J | ISO 6603-2 | 2.5 | 3 |
Thermal properties |
C | Melting temperature | 10 °C/min | °C | ISO 11357-1,-3 | 260 | |
C | Temperature of deflection under load | 1.80 MPa | °C | ISO 75-1,-2 | 235 | |
C | Temperature of deflection under load | 0.45 MPa | °C | ISO 75-1,-2 | 250 | |
| Vicat softening temperature | 50 N; 120 °C/h | °C | ISO 306 | 237 | |
C | Coefficient of linear thermal expansion, parallel | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.2 | |
C | Coefficient of linear thermal expansion, transverse | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.8 | |
Electrical properties (23 °C/50 % r. h.) |
C | Comparative tracking index CTI | Solution A | Rating | IEC 60112 | 525 | |
Other properties (23 °C) |
C | Density | | kg/m³ | ISO 1183 | 1430 | |
| Bulk density | | kg/m³ | ISO 60 | 700 | |
Processing conditions for test specimens |
C | Injection molding-Melt temperature | | °C | ISO 294 | 290 | |
C | Injection molding-Mold temperature | | °C | ISO 294 | 80 | |
Processing recommendations |
| Drying temperature dry air dryer | | °C | - | 80 | |
| Drying time dry air dryer | | h | - | 2-6 | |
| Residual moisture content | | % | Acc. to Karl Fischer | 0.03-0.12 | |
| Melt temperature (Tmin - Tmax) | | °C | - | 270-290 | |
| admissible residence time at Tmax | | min | - | <5 | |
| Mold temperature | | °C | - | 80-100 | |