Rheological properties |
C | Molding shrinkage, parallel | 60x60x2; 260 °C / MT 80 °C; 600 bar | % | ISO 294-4 | 2.2 |
C | Molding shrinkage, transverse | 60x60x2; 260 °C / MT 80 °C; 600 bar | % | ISO 294-4 | 2.0 |
| Post- shrinkage, parallel | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.2 |
| Post- shrinkage, transverse | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.2 |
Mechanical properties (23 °C/50 % r. h.) |
C | Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 4150 |
C | Tensile Stress at break | 5 mm/min | MPa | ISO 527-1,-2 | 40 |
C | Tensile Strain at break | 5 mm/min | % | ISO 527-1,-2 | 1.8 |
C | Charpy impact strength | 23 °C | kJ/m² | ISO 179-1eU | 17 |
C | Charpy impact strength | -30 °C | kJ/m² | ISO 179-1eU | 17 |
C | Charpy notched impact strength | 23 °C | kJ/m² | ISO 179-1eA | <10 |
C | Charpy notched impact strength | -30 °C | kJ/m² | ISO 179-1eA | <10 |
| Izod impact strength | 23 °C | kJ/m² | ISO 180-1U | 15 |
| Izod notched impact strength | 23 °C | kJ/m² | ISO 180-1A | <10 |
| Izod notched impact strength | -30 °C | kJ/m² | ISO 180-1A | <10 |
| Flexural modulus | 2 mm/min | MPa | ISO 178-A | 4200 |
| Flexural strength | 2 mm/min | MPa | ISO 178-A | 70 |
| Flexural strain at flexural strength | 2 mm/min | % | ISO 178-A | 2.3 |
| Ball indentation hardness | | N/mm² | ISO 2039-1 | 160 |
Thermal properties |
C | Melting temperature | 10 °C/min | °C | ISO 11357-1,-3 | 220 |
C | Temperature of deflection under load | 1.80 MPa | °C | ISO 75-1,-2 | 100 |
C | Temperature of deflection under load | 0.45 MPa | °C | ISO 75-1,-2 | 180 |
| Vicat softening temperature | 50 N; 120 °C/h | °C | ISO 306 | 190 |
C | Coefficient of linear thermal expansion, parallel | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.8 |
C | Coefficient of linear thermal expansion, transverse | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.9 |
C | Burning behavior UL 94 | 1.5 mm | Class | UL 94 | V-0 |
C | Burning behavior UL 94 | 0.75 mm | Class | UL 94 | V-0 |
C | Burning behavior UL 94-5V | 3.0 mm | Class | UL 94 | 5VA |
C | Oxygen index | Method A | % | ISO 4589-2 | 41 |
| Resistance to heat (ball pressure test) | | °C | IEC 60695-10-2 | 205 |
| Glow wire test (GWFI) | 0.4 mm | °C | IEC 60695-2-12 | 960 |
| Glow wire test (GWFI) | 0.75 mm | °C | IEC 60695-2-12 | 960 |
| Glow wire test (GWFI) | 1.5 mm | °C | IEC 60695-2-12 | 960 |
| Glow wire test (GWFI) | 3.0 mm | °C | IEC 60695-2-12 | 960 |
Electrical properties (23 °C/50 % r. h.) |
C | Electric strength | 1 mm | kV/mm | IEC 60243-1 | 28 |
C | Comparative tracking index CTI | Solution A | Rating | IEC 60112 | 400 |
| Comparative tracking index CTI | Solution A | PLC | UL 746A | 1 |
Other properties (23 °C) |
C | Water absorption (Saturation value) | Water at 23 °C | % | ISO 62 | 0.4 |
C | Water absorption (Equilibrium value) | 23 °C; 50 % RH | % | ISO 62 | 0.2 |
C | Density | | kg/m³ | ISO 1183 | 1520 |
| Bulk density | | kg/m³ | ISO 60 | 800 |
Processing conditions for test specimens |
C | Injection molding-Melt temperature | | °C | ISO 294 | 260 |
C | Injection molding-Mold temperature | | °C | ISO 294 | 80 |
Processing recommendations |
| Drying temperature circulating air dryer | | °C | - | 120 |
| Drying time circulating air dryer | | h | - | 4-8 |
| Residual moisture content | | % | Acc. to Karl Fischer | 0.02 |
| Melt temperature (Tmin - Tmax) | | °C | - | 250-270 |
| admissible residence time at Tmax | | min | - | <5 |
| Mold temperature | | °C | - | 70-90 |