Durethan BKV30FN34 000000

  _More Info 
  _Data sheet ISO (PDF) 


Data sheet

PA 6, 30% glass fibers, injection molding, halogen free flame retardant
ISO Shortname:  ISO 16396-PA 6,GF30 FR(30+40),GF2HR,S14-110
PropertyTest ConditionUnitStandardguide value1
Rheological properties
CMolding shrinkage, parallel60x60x2%ISO 294-40.3
CMolding shrinkage, transverse60x60x2%ISO 294-40.7
Post- shrinkage, parallel60x60x2%ISO 294-40.1
Post- shrinkage, transverse60x60x2%ISO 294-40.1

Mechanical properties (23 °C/50 % r. h.)
CTensile modulus1 mm/minMPaISO 527-1,-2115007800
CTensile Stress at break5 mm/minMPaISO 527-1,-214090
CTensile Strain at break5 mm/min%ISO 527-1,-22.85.4
CCharpy impact strength23 °CkJ/m²ISO 179-1eU6065
CCharpy impact strength-30 °CkJ/m²ISO 179-1eU6055
CCharpy notched impact strength23 °CkJ/m²ISO 179-1eA<1013
CCharpy notched impact strength-30 °CkJ/m²ISO 179-1eA<10<10
Izod impact strength23 °CkJ/m²ISO 180-1U5560
Izod notched impact strength23 °CkJ/m²ISO 180-1A1014
Flexural modulus2 mm/minMPaISO 178-A115008000
Flexural strength2 mm/minMPaISO 178-A230160
Flexural strain at flexural strength2 mm/min%ISO 178-A2.84.5
Flexural stress at 3.5 % strain2 mm/minMPaISO 178-A150
Ball indentation hardnessN/mm²ISO 2039-1245150

Thermal properties
CMelting temperature10 °C/min°CISO 11357-1,-3220
CTemperature of deflection under load1.80 MPa°CISO 75-1,-2205
CTemperature of deflection under load0.45 MPa°CISO 75-1,-2215
Vicat softening temperature50 N; 120 °C/h°CISO 306210
CCoefficient of linear thermal expansion, parallel23 to 55 °C10-4/KISO 11359-1,-20.2
CCoefficient of linear thermal expansion, transverse23 to 55 °C10-4/KISO 11359-1,-20.7
CBurning behavior UL 941.5 mmClassUL 94V-0
CBurning behavior UL 940.75 mmClassUL 94V-0
CBurning behavior UL 94-5V1.5 mmClassUL 945VA
Resistance to heat (ball pressure test)°CIEC 60695-10-2211
Glow wire test (GWFI)0.75 mm°CIEC 60695-2-12960
Glow wire test (GWFI)1.5 mm°CIEC 60695-2-12960
Glow wire test (GWFI)3.0 mm°CIEC 60695-2-12960
Glow wire test (GWIT)0.75 mm°CIEC 60695-2-13775
Glow wire test (GWIT)1.5 mm°CIEC 60695-2-13775
Glow wire test (GWIT)3.0 mm°CIEC 60695-2-13800

Electrical properties (23 °C/50 % r. h.)
CRelative permittivity100 Hz-IEC 602503.15.0
CRelative permittivity1 MHz-IEC 602504.04.0
CDissipation factor100 Hz10-4IEC 60250150710
CDissipation factor1 MHz10-4IEC 60250190570
CVolume resistivityOhm·mIEC 62631-32.7E+131.3E+10
CElectric strength1 mmkV/mmIEC 60243-13231
CComparative tracking index CTISolution ARatingIEC 60112600
Comparative tracking index CTISolution APLCUL 746A0

Other properties (23 °C)
CWater absorption (Saturation value)Water at 23 °C%ISO 625.2
CWater absorption (Equilibrium value)23 °C; 50 % RH%ISO 621.6
CDensitykg/m³ISO 11831463
Bulk densitykg/m³ISO 60650

Processing conditions for test specimens
CInjection molding-Melt temperature°CISO 294260
CInjection molding-Mold temperature°CISO 29480

Processing recommendations
Drying temperature dry air dryer°C -80
Drying time dry air dryerh -4
Residual moisture content%Acc. to Karl Fischer 0,03-0,07
Melt temperature (Tmin - Tmax)°C -250-270
Mold temperature°C -70-90

1Typical properties: these are not to be construed as specifications
CThese property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Disclaimer for trial products
This is a trial product at the developmental stage. No definitive statements can therefore be made as to type conformity, processability, long-term performance characteristics or other production or application parameters. Therefore, the purchaser/user uses the trial product entirely at his own risk without having been given any warranty or guarantee and agrees that the supplier shall not be liable for any damage, of whatever nature, arising out of such use. Unless specified to the contrary, the values given have been established on standardized test specimens at room temperature. The figures should be regarded as non-binding approximate data only, and not as guide values or binding minimum values. Please note that, under certain conditions, the properties can be affected to a considerable extent by the design of the mold/die, the processing conditions and the coloring. The marketing and continued supply of this material are not assured and may be discontinued at any time. Our products are sold in accordance with the current version of our General Conditions of Sale and Delivery.
Processing note
Under the recommended processing conditions small quantities of decomposition product may be given off during processing. To preclude any risk to the health and well-being of the machine operatives, tolerance limits for the work environment must be ensured by the provision of efficient exhaust ventilation and fresh air at the workplace in accordance with the Safety Data Sheet. In order to prevent the partial decomposition of the polymer and the generation of volatile decomposition products, the prescribed processing temperatures should not be substantially exceeded. Since excessively high temperatures are generally the result of operator error or defects in the heating system, special care and controls are essential in these areas.
Conditioning in accordance with ISO 1110 (70 °C; 62 % r.h.)
Envalior Deutschland GmbH | D-50569 COLOGNE
Date: 17.08.2023