Rheological properties |
C | Molding shrinkage, parallel | 60x60x2 | % | ISO 294-4 | 0.7 | |
C | Molding shrinkage, transverse | 60x60x2 | % | ISO 294-4 | 0.6 | |
| Post- shrinkage, parallel | 60x60x2 | % | ISO 294-4 | 0.1 | |
| Post- shrinkage, transverse | 60x60x2 | % | ISO 294-4 | 0.1 | |
Mechanical properties (23 °C/50 % r. h.) |
C | Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 13600 | 5000 |
C | Tensile Stress at break | 5 mm/min | MPa | ISO 527-1,-2 | 95 | 60 |
C | Tensile Strain at break | 5 mm/min | % | ISO 527-1,-2 | 2.8 | 5 |
C | Charpy impact strength | 23 °C | kJ/m² | ISO 179-1eU | 35 | 50 |
C | Charpy impact strength | -30 °C | kJ/m² | ISO 179-1eU | 20 | 20 |
C | Charpy notched impact strength | 23 °C | kJ/m² | ISO 179-1eA | <10 | <10 |
C | Charpy notched impact strength | -30 °C | kJ/m² | ISO 179-1eA | <10 | <10 |
| Izod impact strength | 23 °C | kJ/m² | ISO 180-1U | 35 | 20 |
| Izod impact strength | -30 °C | kJ/m² | ISO 180-1U | 20 | 20 |
| Izod notched impact strength | 23 °C | kJ/m² | ISO 180-1A | <10 | <10 |
| Izod notched impact strength | -30 °C | kJ/m² | ISO 180-1A | <10 | <10 |
| Flexural modulus | 2 mm/min | MPa | ISO 178-A | 14000 | 6000 |
| Flexural strength | 2 mm/min | MPa | ISO 178-A | 180 | 110 |
| Flexural strain at flexural strength | 2 mm/min | % | ISO 178-A | 3 | 4 |
| Flexural stress at 3.5 % strain | 2 mm/min | MPa | ISO 178-A | | 100 |
| Ball indentation hardness | | N/mm² | ISO 2039-1 | 410 | 229 |
Thermal properties |
C | Melting temperature | 10 °C/min | °C | ISO 11357-1,-3 | 222 | |
C | Temperature of deflection under load | 1.80 MPa | °C | ISO 75-1,-2 | 142 | |
C | Temperature of deflection under load | 0.45 MPa | °C | ISO 75-1,-2 | 191 | |
| Vicat softening temperature | 50 N; 120 °C/h | °C | ISO 306 | 208 | |
C | Coefficient of linear thermal expansion, parallel | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.4 | |
C | Coefficient of linear thermal expansion, transverse | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.4 | |
| Thermal conductivity, in-plane | | W/(m·K) | ISO 22007-4 | 1.8 | |
| Thermal conductivity, through-plane | | W/(m·K) | ISO 22007-4 | 1.7 | |
C | Burning behavior UL 94 | 0.75 mm | Class | UL 94 | HB | |
Electrical properties (23 °C/50 % r. h.) |
C | Volume resistivity | | Ohm·m | IEC 62631-3 | 1.40E+13 | |
C | Surface resistivity | | Ohm | IEC 62631-3 | 6.60E+13 | |
C | Electric strength | 1 mm | kV/mm | IEC 60243-1 | 31 | |
C | Comparative tracking index CTI | Solution A | Rating | IEC 60112 | 600 | |
Other properties (23 °C) |
C | Density | | kg/m³ | ISO 1183 | 2510 | |
| Bulk density | | kg/m³ | ISO 60 | 1374 | |
Processing conditions for test specimens |
C | Injection molding-Melt temperature | | °C | ISO 294 | 290 | |
C | Injection molding-Mold temperature | | °C | ISO 294 | 80 | |
Processing recommendations |
| Drying temperature dry air dryer | | °C | - | 80 | |
| Drying time dry air dryer | | h | - | 2-6 | |
| Melt temperature (Tmin - Tmax) | | °C | - | 280-300 | |
| Mold temperature | | °C | - | 80-120 | |