Rheological properties |
C | Molding shrinkage, parallel | 60x60x2; 280 °C / MT 80 °C; 600 bar | % | ISO 294-4 | 0.19 | |
C | Molding shrinkage, transverse | 60x60x2; 280 °C / MT 80 °C; 600 bar | % | ISO 294-4 | 0.6 | |
| Post- shrinkage, parallel | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.04 | |
| Post- shrinkage, transverse | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.08 | |
Mechanical properties (23 °C/50 % r. h.) |
C | Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 16200 | 10000 |
C | Tensile Stress at break | 5 mm/min | MPa | ISO 527-1,-2 | 215 | 140 |
C | Tensile Strain at break | 5 mm/min | % | ISO 527-1,-2 | 2.7 | 3.5 |
C | Charpy impact strength | 23 °C | kJ/m² | ISO 179-1eU | 100 | 85 |
C | Charpy impact strength | -30 °C | kJ/m² | ISO 179-1eU | 95 | 85 |
| Izod impact strength | 23 °C | kJ/m² | ISO 180-1U | 85 | 80 |
| Izod impact strength | -30 °C | kJ/m² | ISO 180-1U | 85 | 80 |
| Izod notched impact strength | 23 °C | kJ/m² | ISO 180-1A | 17 | 20 |
| Izod notched impact strength | -30 °C | kJ/m² | ISO 180-1A | 15 | |
| Flexural modulus | 2 mm/min | MPa | ISO 178-A | 15000 | 9900 |
| Flexural strength | 2 mm/min | MPa | ISO 178-A | 340 | 230 |
| Flexural strain at flexural strength | 2 mm/min | % | ISO 178-A | 3.1 | 4.4 |
C | Puncture maximum force | 23 °C | N | ISO 6603-2 | 1179 | |
C | Puncture maximum force | -30 °C | N | ISO 6603-2 | 1000 | |
C | Puncture energy | 23 °C | J | ISO 6603-2 | 4.3 | |
C | Puncture energy | -30 °C | J | ISO 6603-2 | 3.4 | |
| Ball indentation hardness | | N/mm² | ISO 2039-1 | 232 | |
Thermal properties |
C | Melting temperature | 10 °C/min | °C | ISO 11357-1,-3 | 222 | |
C | Temperature of deflection under load | 1.80 MPa | °C | ISO 75-1,-2 | 210 | |
C | Temperature of deflection under load | 0.45 MPa | °C | ISO 75-1,-2 | 220 | |
C | Temperature of deflection under load | 8.00 MPa | °C | ISO 75-1,-2 | 180 | |
| Vicat softening temperature | 50 N; 120 °C/h | °C | ISO 306 | 214 | |
C | Coefficient of linear thermal expansion, parallel | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.12 | |
C | Coefficient of linear thermal expansion, transverse | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.9 | |
Electrical properties (23 °C/50 % r. h.) |
C | Relative permittivity | 100 Hz | - | IEC 60250 | 4.7 | 12.9 |
C | Relative permittivity | 1 MHz | - | IEC 60250 | 4.2 | 4.8 |
C | Dissipation factor | 100 Hz | 10-4 | IEC 60250 | 135 | 2622 |
C | Dissipation factor | 1 MHz | 10-4 | IEC 60250 | 170 | 774 |
C | Volume resistivity | | Ohm·m | IEC 62631-3 | 7E12 | 4E9 |
C | Electric strength | 1 mm | kV/mm | IEC 60243-1 | 35 | 34 |
C | Comparative tracking index CTI | Solution A | Rating | IEC 60112 | 400 | |
Other properties (23 °C) |
C | Water absorption (Saturation value) | Water at 23 °C | % | ISO 62 | 5 | |
C | Water absorption (Equilibrium value) | 23 °C; 50 % RH | % | ISO 62 | 1.5 | |
C | Density | | kg/m³ | ISO 1183 | 1570 | |
| Bulk density | | kg/m³ | ISO 60 | 700 | |
Processing conditions for test specimens |
C | Injection molding-Melt temperature | | °C | ISO 294 | 280 | |
C | Injection molding-Mold temperature | | °C | ISO 294 | 80 | |
Processing recommendations |
| Drying temperature dry air dryer | | °C | - | 80 | |
| Drying time dry air dryer | | h | - | 2-6 | |
| Residual moisture content | | % | Acc. to Karl Fischer | 0.03-0.12 | |
| Melt temperature (Tmin - Tmax) | | °C | - | 270-290 | |
| Mold temperature | | °C | - | 80-120 | |