Rheological properties |
C | Molding shrinkage, parallel | 60x60x2; 290 °C / MT 80 °C; 600 bar | % | ISO 294-4 | 0.37 | |
C | Molding shrinkage, transverse | 60x60x2; 290 °C / MT 80 °C; 600 bar | % | ISO 294-4 | 0.93 | |
| Post- shrinkage, parallel | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.05 | |
| Post- shrinkage, transverse | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.09 | |
Mechanical properties (23 °C/50 % r. h.) |
C | Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 16000 | |
C | Tensile Stress at break | 5 mm/min | MPa | ISO 527-1,-2 | 230 | |
C | Tensile Strain at break | 5 mm/min | % | ISO 527-1,-2 | 2.5 | |
C | Charpy impact strength | 23 °C | kJ/m² | ISO 179-1eU | 100 | |
C | Charpy impact strength | -30 °C | kJ/m² | ISO 179-1eU | 100 | |
C | Charpy notched impact strength | 23 °C | kJ/m² | ISO 179-1eA | 17 | |
C | Charpy notched impact strength | -30 °C | kJ/m² | ISO 179-1eA | 15 | |
| Charpy notched impact strength | -40 °C | kJ/m² | ISO 179-1eA | 14 | |
| Izod impact strength | 23 °C | kJ/m² | ISO 180-1U | 90 | |
| Izod impact strength | -30 °C | kJ/m² | ISO 180-1U | 90 | |
| Izod notched impact strength | 23 °C | kJ/m² | ISO 180-1A | 15 | |
| Izod notched impact strength | -30 °C | kJ/m² | ISO 180-1A | 13 | |
| Flexural modulus | 2 mm/min | MPa | ISO 178-A | 15300 | |
| Flexural strength | 2 mm/min | MPa | ISO 178-A | 360 | |
| Flexural strain at flexural strength | 2 mm/min | % | ISO 178-A | 3.0 | |
Thermal properties |
C | Melting temperature | 10 °C/min | °C | ISO 11357-1,-3 | 262 | |
C | Temperature of deflection under load | 1.80 MPa | °C | ISO 75-1,-2 | 250 | |
C | Temperature of deflection under load | 0.45 MPa | °C | ISO 75-1,-2 | 250 | |
C | Burning behavior UL 94 | 1.5 mm | Class | UL 94 | HB | |
C | Burning behavior UL 94 | 0.75 mm | Class | UL 94 | HB | |
Electrical properties (23 °C/50 % r. h.) |
C | Relative permittivity | 100 Hz | - | IEC 60250 | 5.0 | |
C | Relative permittivity | 1 MHz | - | IEC 60250 | 4.4 | |
C | Dissipation factor | 100 Hz | 10-4 | IEC 60250 | 250 | |
C | Dissipation factor | 1 MHz | 10-4 | IEC 60250 | 230 | |
C | Volume resistivity | | Ohm·m | IEC 62631-3 | 1E13 | |
C | Surface resistivity | | Ohm | IEC 62631-3 | 1E16 | |
C | Electric strength | 1 mm | kV/mm | IEC 60243-1 | 38 | |
C | Comparative tracking index CTI | Solution A | Rating | IEC 60112 | 600 | |
Other properties (23 °C) |
C | Density | | kg/m³ | ISO 1183 | 1570 | |
| Bulk density | | kg/m³ | ISO 60 | 700 | |
Processing conditions for test specimens |
C | Injection molding-Melt temperature | | °C | ISO 294 | 290 | |
C | Injection molding-Mold temperature | | °C | ISO 294 | 80 | |
Processing recommendations |
| Drying temperature dry air dryer | | °C | - | 80 | |
| Drying time dry air dryer | | h | - | 2-6 | |
| Residual moisture content | | % | Acc. to Karl Fischer | 0.03-0.12 | |
| Melt temperature (Tmin - Tmax) | | °C | - | 280-300 | |
| Mold temperature | | °C | - | 80-120 | |