Rheological properties |
C | Molding shrinkage, parallel | 60x60x2; 280 °C / MT 80 °C; 600 bar | % | ISO 294-4 | 0.25 | |
C | Molding shrinkage, transverse | 60x60x2; 280 °C / MT 80 °C; 600 bar | % | ISO 294-4 | 0.35 | |
| Post- shrinkage, parallel | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.05 | |
| Post- shrinkage, transverse | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.10 | |
Mechanical properties (23 °C/50 % r. h.) |
C | Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 20000 | 12500 |
C | Tensile Stress at break | 5 mm/min | MPa | ISO 527-1,-2 | 230 | 155 |
C | Tensile Strain at break | 5 mm/min | % | ISO 527-1,-2 | 2.5 | 3.5 |
C | Charpy impact strength | 23 °C | kJ/m² | ISO 179-1eU | 95 | |
C | Charpy impact strength | -30 °C | kJ/m² | ISO 179-1eU | 95 | |
C | Charpy notched impact strength | 23 °C | kJ/m² | ISO 179-1eA | 17 | |
C | Charpy notched impact strength | -30 °C | kJ/m² | ISO 179-1eA | 17 | |
| Izod impact strength | 23 °C | kJ/m² | ISO 180-1U | 90 | 90 |
| Izod impact strength | -30 °C | kJ/m² | ISO 180-1U | 90 | 90 |
| Izod notched impact strength | 23 °C | kJ/m² | ISO 180-1A | 18 | |
| Izod notched impact strength | -30 °C | kJ/m² | ISO 180-1A | 18 | |
| Flexural modulus | 2 mm/min | MPa | ISO 178-A | 20200 | |
| Flexural strength | 2 mm/min | MPa | ISO 178-A | 390 | |
| Flexural strain at flexural strength | 2 mm/min | % | ISO 178-A | 3.0 | |
C | Puncture maximum force | 23 °C | N | ISO 6603-2 | 1370 | |
C | Puncture maximum force | -30 °C | N | ISO 6603-2 | 1300 | |
C | Puncture energy | 23 °C | J | ISO 6603-2 | 4.3 | |
C | Puncture energy | -30 °C | J | ISO 6603-2 | 3.7 | |
Thermal properties |
C | Melting temperature | 10 °C/min | °C | ISO 11357-1,-3 | 221 | |
C | Temperature of deflection under load | 1.80 MPa | °C | ISO 75-1,-2 | 213 | |
C | Temperature of deflection under load | 0.45 MPa | °C | ISO 75-1,-2 | 222 | |
C | Coefficient of linear thermal expansion, parallel | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.1 | |
C | Coefficient of linear thermal expansion, transverse | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.8 | |
Other properties (23 °C) |
C | Density | | kg/m³ | ISO 1183 | 1700 | |
Processing conditions for test specimens |
C | Injection molding-Melt temperature | | °C | ISO 294 | 280 | |
C | Injection molding-Mold temperature | | °C | ISO 294 | 80 | |
Processing recommendations |
| Drying temperature dry air dryer | | °C | - | 80 | |
| Drying time dry air dryer | | h | - | 2-6 | |
| Residual moisture content | | % | Acc. to Karl Fischer | 0.05-0.15 | |
| Melt temperature (Tmin - Tmax) | | °C | - | 270-290 | |
| Mold temperature | | °C | - | 80-120 | |