Rheological properties |
C | Molding shrinkage, parallel | 60x60x2; 280 °C / MT 80 °C; 600 bar | % | ISO 294-4 | 0.25 | |
C | Molding shrinkage, transverse | 60x60x2; 280 °C / MT 80 °C; 600 bar | % | ISO 294-4 | 0.65 | |
| Post- shrinkage, parallel | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.1 | |
| Post- shrinkage, transverse | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.15 | |
Mechanical properties (23 °C/50 % r. h.) |
C | Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 9000 | 5200 |
C | Tensile Stress at break | 5 mm/min | MPa | ISO 527-1,-2 | 160 | 100 |
C | Tensile Strain at break | 5 mm/min | % | ISO 527-1,-2 | 4 | 7 |
C | Charpy impact strength | 23 °C | kJ/m² | ISO 179-1eU | 95 | 110 |
C | Charpy impact strength | -30 °C | kJ/m² | ISO 179-1eU | 80 | 80 |
C | Charpy notched impact strength | 23 °C | kJ/m² | ISO 179-1eA | 15 | 25 |
C | Charpy notched impact strength | -30 °C | kJ/m² | ISO 179-1eA | 10 | 10 |
| Izod impact strength | 23 °C | kJ/m² | ISO 180-1U | 85 | 100 |
| Izod impact strength | -30 °C | kJ/m² | ISO 180-1U | 75 | 75 |
| Izod notched impact strength | 23 °C | kJ/m² | ISO 180-1A | 15 | 25 |
| Izod notched impact strength | -30 °C | kJ/m² | ISO 180-1A | 10 | 10 |
| Flexural modulus | 2 mm/min | MPa | ISO 178-A | 8000 | 4800 |
| Flexural strength | 2 mm/min | MPa | ISO 178-A | 255 | 145 |
| Flexural strain at flexural strength | 2 mm/min | % | ISO 178-A | 4.5 | 7 |
| Flexural stress at 3.5 % strain | 2 mm/min | MPa | ISO 178-A | 240 | 115 |
Thermal properties |
C | Melting temperature | 10 °C/min | °C | ISO 11357-1,-3 | 220 | |
C | Temperature of deflection under load | 1.80 MPa | °C | ISO 75-1,-2 | 200 | |
C | Temperature of deflection under load | 0.45 MPa | °C | ISO 75-1,-2 | 215 | |
| Vicat softening temperature | 50 N; 120 °C/h | °C | ISO 306 | >200 | |
C | Coefficient of linear thermal expansion, parallel | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.2 | |
C | Coefficient of linear thermal expansion, transverse | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 1.1 | |
Other properties (23 °C) |
C | Density | | kg/m³ | ISO 1183 | 1355 | |
| Bulk density | | kg/m³ | ISO 60 | 700 | |
Processing conditions for test specimens |
C | Injection molding-Melt temperature | | °C | ISO 294 | 280 | |
C | Injection molding-Mold temperature | | °C | ISO 294 | 80 | |
Processing recommendations |
| Drying temperature dry air dryer | | °C | - | 80 | |
| Drying time dry air dryer | | h | - | 2-6 | |
| Residual moisture content | | % | Acc. to Karl Fischer | 0.03-0.12 | |
| Melt temperature (Tmin - Tmax) | | °C | - | 260-290 | |
| Mold temperature | | °C | - | 80-100 | |