Data sheet

Durethan AKV35HRH2.0 901510


 
PA 66, 35 % glass fibers, injection molding, heat-aging stabilized, hydrolysis stabilized
 
ISO/ ASTM
 
ISO Shortname:  ISO 16396-PA 66,GF35,GHRW,S14-110
PropertyTest ConditionUnitStandardguide value
 d.a.m.cond.
Rheological properties
CMolding shrinkage, parallel60x60x2; 290 °C / MT 80 °C; 600 bar%ISO 294-40.38
CMolding shrinkage, transverse60x60x2; 290 °C / MT 80 °C; 600 bar%ISO 294-41.05
Post- shrinkage, parallel60x60x2; 120 °C; 4 h%ISO 294-40.06
Post- shrinkage, transverse60x60x2; 120 °C; 4 h%ISO 294-40.09

Mechanical properties (23 °C/50 % r. h.)
CTensile modulus1 mm/minMPaISO 527-1,-2115007800
CTensile Stress at break5 mm/minMPaISO 527-1,-2195135
CTensile Strain at break5 mm/min%ISO 527-1,-23.16.0
CCharpy impact strength23 °CkJ/m²ISO 179-1eU8585
CCharpy impact strength-30 °CkJ/m²ISO 179-1eU7580
CCharpy notched impact strength23 °CkJ/m²ISO 179-1eA1320
CCharpy notched impact strength-30 °CkJ/m²ISO 179-1eA< 10< 10
Charpy notched impact strength-40 °CkJ/m²ISO 179-1eA< 10< 10
Izod impact strength23 °CkJ/m²ISO 180-1U75
Izod impact strength-30 °CkJ/m²ISO 180-1U65
Izod notched impact strength23 °CkJ/m²ISO 180-1A<10<10
Izod notched impact strength-30 °CkJ/m²ISO 180-1A1010
Flexural modulus2 mm/minMPaISO 178-A107007000
Flexural strength2 mm/minMPaISO 178-A305210
Flexural strain at flexural strength2 mm/min%ISO 178-A3.86.0
Flexural stress at 3.5 % strain2 mm/minMPaISO 178-A180

Thermal properties
CMelting temperature10 °C/min°CISO 11357-1,-3262
CTemperature of deflection under load1.80 MPa°CISO 75-1,-2245
CTemperature of deflection under load0.45 MPa°CISO 75-1,-2250
Vicat softening temperature50 N; 120 °C/h°CISO 306255
CCoefficient of linear thermal expansion, parallel23 to 55 °C10-4/KISO 11359-1,-20.2
CCoefficient of linear thermal expansion, transverse23 to 55 °C10-4/KISO 11359-1,-20.8
CBurning behavior UL 941.5 mmClassUL 94HB
COxygen indexMethod A%ISO 4589-226
Glow wire test (GWFI)2.0 mm°CIEC 60695-2-12650
Burning behavior US-FMVSS302>=1.0 mm ISO 3795passed
CVicat softening temperature50 N; 50 °C/h°CISO 306> 230

Electrical properties (23 °C/50 % r. h.)
CRelative permittivity100 Hz-IEC 602503.9
CRelative permittivity1 MHz-IEC 602503.6
CDissipation factor100 Hz10-4IEC 60250100
CDissipation factor1 MHz10-4IEC 60250150
CVolume resistivityOhm·mIEC 600931E13
CSurface resistivityOhmIEC 600931E14
CElectric strength1 mmkV/mmIEC 60243-135
CComparative tracking index CTISolution ARatingIEC 60112425

Other properties (23 °C)
CWater absorption (Saturation value)Water at 23 °C%ISO 625.2
CWater absorption (Equilibrium value)23 °C; 50 % RH%ISO 621.7
CDensitykg/m³ISO 11831410

Processing conditions for test specimens
CInjection molding-Melt temperature°CISO 294290
CInjection molding-Mold temperature°CISO 29480

Processing recommendations
Drying temperature dry air dryer°C -80
Drying time dry air dryerh -2-6
Melt temperature (Tmin - Tmax)°C -280-300
Mold temperature°C -80-120
CThese property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Disclaimer
Disclaimer for commercial products
This information and our technical advice - whether verbal, in writing or by way of trials - are given in good faith but without warranty, and this also applies where proprietary rights of third parties are involved. Our advice does not release you from the obligation to verify the information currently provided - especially that contained in our safety data and technical information sheets - and to test our products as to their suitability for the intended processes and uses. The application, use and processing of our products and the products manufactured by you on the basis of our technical advice are beyond our control and, therefore, entirely your own responsibility. Our products are sold in accordance with the current version of our General Conditions of Sale and Delivery.
Test values
Unless specified to the contrary, the values given have been established on standardized test specimens at room temperature. The figures should be regarded as guide values only and not as binding minimum values. Kindly note that, under certain conditions, the properties can be affected to a considerable extent by the design of the mould/die, the processing conditions and the coloring.
Processing note
Under the recommended processing conditions small quantities of decomposition product may be given off during processing. To preclude any risk to the health and well-being of the machine operatives, tolerance limits for the work environment must be ensured by the provision of efficient exhaust ventilation and fresh air at the workplace in accordance with the Safety Data Sheet. In order to prevent the partial decomposition of the polymer and the generation of volatile decomposition products, the prescribed processing temperatures should not be substantially exceeded. Since excessively high temperatures are generally the result of operator error or defects in the heating system, special care and controls are essential in these areas.
Conditioning
Conditioning in accordance with ISO 1110 (70 °C; 62 % r.h.)