Durethan BKV60H3.0EF 900116

PA 6, 60 % glass fibers, injection molding, improved flowability, heat-aging stabilized
ISO Shortname:  ISO 16396-PA 6,GF60,GHR,S10-220
PropertyTest ConditionUnitStandardguide value
Rheological properties
CMolding shrinkage, parallel60x60x2; 280 °C / MT 80 °C; 600 bar%ISO 294-40.3
CMolding shrinkage, transverse60x60x2; 280 °C / MT 80 °C; 600 bar%ISO 294-40.5
Post- shrinkage, parallel60x60x2; 120 °C; 4 h%ISO 294-40.05
Post- shrinkage, transverse60x60x2; 120 °C; 4 h%ISO 294-40.05

Mechanical properties (23 °C/50 % r. h.)
CTensile modulus1 mm/minMPaISO 527-1,-22000012500
CTensile Stress at break5 mm/minMPaISO 527-1,-2230158
CTensile Strain at break5 mm/min%ISO 527-1,-22.53.5
CCharpy impact strength23 °CkJ/m²ISO 179-1eU9595
CCharpy impact strength-30 °CkJ/m²ISO 179-1eU9595
CCharpy notched impact strength23 °CkJ/m²ISO 179-1eA1724
CCharpy notched impact strength-30 °CkJ/m²ISO 179-1eA17
Izod impact strength23 °CkJ/m²ISO 180-1U9090
Izod impact strength-30 °CkJ/m²ISO 180-1U9090
Izod notched impact strength23 °CkJ/m²ISO 180-1A1825
Izod notched impact strength-30 °CkJ/m²ISO 180-1A18
Flexural modulus2 mm/minMPaISO 178-A2020013500
Flexural strength2 mm/minMPaISO 178-A390250
Flexural strain at flexural strength2 mm/min%ISO 178-A34
Flexural stress at 3.5 % strain2 mm/minMPaISO 178-A245
CPuncture maximum force23 °CNISO 6603-21300
CPuncture maximum force-30 °CNISO 6603-21200
CPuncture energy23 °CJISO 6603-24.5
CPuncture energy-30 °CJISO 6603-23.8

Thermal properties
CMelting temperature10 °C/min°CISO 11357-1,-3221
CTemperature of deflection under load1.80 MPa°CISO 75-1,-2213
CTemperature of deflection under load0.45 MPa°CISO 75-1,-2220
CCoefficient of linear thermal expansion, parallel23 to 55 °C10-4/KISO 11359-1,-20.1
CCoefficient of linear thermal expansion, transverse23 to 55 °C10-4/KISO 11359-1,-20.8
Glow wire test (GWFI)0.75 mm°CIEC 60695-2-12700
Glow wire test (GWFI)1.5 mm°CIEC 60695-2-12725
Glow wire test (GWFI)3.0 mm°CIEC 60695-2-12825
Glow wire test (GWIT)0.75 mm°CIEC 60695-2-13725
Glow wire test (GWIT)1.5 mm°CIEC 60695-2-13750
Glow wire test (GWIT)3.0 mm°CIEC 60695-2-13750

Electrical properties (23 °C/50 % r. h.)
CRelative permittivity100 Hz-IEC 602504.38.71
CRelative permittivity1 MHz-IEC 602505.074.68
CDissipation factor100 Hz10-4IEC 602500.020.1
CDissipation factor1 MHz10-4IEC 602500.030.06
CVolume resistivityOhm·mIEC 600936.14E+126.60E+10
CSurface resistivityOhmIEC 600935.82E+142.64E+14
CElectric strength1 mmkV/mmIEC 60243-128.625.8
CComparative tracking index CTISolution ARatingIEC 60112575

Other properties (23 °C)
CDensitykg/m³ISO 11831710
Bulk densitykg/m³ISO 60750

Processing conditions for test specimens
CInjection molding-Melt temperature°CISO 294280
CInjection molding-Mold temperature°CISO 29480

Processing recommendations
Drying temperature dry air dryer°C -80
Drying time dry air dryerh -2-6
Residual moisture content%Acc. to Karl Fischer 0.05-0.15
Melt temperature (Tmin - Tmax)°C -270-290
Mold temperature°C -80-120
CThese property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Disclaimer for commercial products
This information and our technical advice - whether verbal, in writing or by way of trials - are given in good faith but without warranty, and this also applies where proprietary rights of third parties are involved. Our advice does not release you from the obligation to verify the information currently provided - especially that contained in our safety data and technical information sheets - and to test our products as to their suitability for the intended processes and uses. The application, use and processing of our products and the products manufactured by you on the basis of our technical advice are beyond our control and, therefore, entirely your own responsibility. Our products are sold in accordance with the current version of our General Conditions of Sale and Delivery.
Test values
Unless specified to the contrary, the values given have been established on standardized test specimens at room temperature. The figures should be regarded as guide values only and not as binding minimum values. Kindly note that, under certain conditions, the properties can be affected to a considerable extent by the design of the mould/die, the processing conditions and the coloring.
Processing note
Under the recommended processing conditions small quantities of decomposition product may be given off during processing. To preclude any risk to the health and well-being of the machine operatives, tolerance limits for the work environment must be ensured by the provision of efficient exhaust ventilation and fresh air at the workplace in accordance with the Safety Data Sheet. In order to prevent the partial decomposition of the polymer and the generation of volatile decomposition products, the prescribed processing temperatures should not be substantially exceeded. Since excessively high temperatures are generally the result of operator error or defects in the heating system, special care and controls are essential in these areas.
Conditioning in accordance with ISO 1110 (70 °C; 62 % r.h.)
Date: 07.08.2019