Pocan B3233HRE 000000
  _More Info 
  _Data sheet ISO (PDF) 

 

Data sheet
PBT, 30% glass fibers, injection molding, improved flowability, hydrolysis stabilized, improved electrical tracking resistance (CTI600)
 
ISO Shortname:  ISO 20028-PBT,GF30,GHMRW,09-100
PropertyTest ConditionUnitStandardguide value1
Rheological properties
CMelt volume-flow rate260 °C; 2.16 kgcm³/(10 min)ISO 1133-115
CMolding shrinkage, parallel60x60x2; 600 bar%ISO 294-40.4
CMolding shrinkage, transverse60x60x2; 600 bar%ISO 294-41
Post- shrinkage, parallel60x60x2; 120 °C; 4 h%ISO 294-40.1
Post- shrinkage, transverse60x60x2; 120 °C; 4 h%ISO 294-40.1

Mechanical properties (23 °C/50 % r. h.)
CTensile modulus1 mm/minMPaISO 527-1,-29700
CTensile Stress at break5 mm/minMPaISO 527-1,-2120
CTensile Strain at break5 mm/min%ISO 527-1,-22.6
CCharpy impact strength23 °CkJ/m²ISO 179-1eU60
CCharpy impact strength-30 °CkJ/m²ISO 179-1eU60
CCharpy notched impact strength23 °CkJ/m²ISO 179-1eA<10
CCharpy notched impact strength-30 °CkJ/m²ISO 179-1eA<10
Izod impact strength23 °CkJ/m²ISO 180-1C50
Izod notched impact strength23 °CkJ/m²ISO 180-1A10
Flexural modulus2 mm/minMPaISO 178-A9200
Flexural strength2 mm/minMPaISO 178-A190
Flexural strain at flexural strength2 mm/min%ISO 178-A2.9

Thermal properties
CMelting temperature10 °C/min°CISO 11357-1,-3225
CTemperature of deflection under load1.80 MPa°CISO 75-1,-2202
CTemperature of deflection under load0.45 MPa°CISO 75-1,-2220
CTemperature of deflection under load8.00 MPa°CISO 75-1,-2206
CCoefficient of linear thermal expansion, parallel23 to 55 °C10-4/KISO 11359-1,-20.2
CCoefficient of linear thermal expansion, transverse23 to 55 °C10-4/KISO 11359-1,-21.3

Electrical properties (23 °C/50 % r. h.)
CComparative tracking index CTISolution ARatingIEC 60112600

Other properties (23 °C)
CDensitykg/m³ISO 11831530
Bulk densitykg/m³ISO 60770

Processing conditions for test specimens
CInjection molding-Melt temperature°CISO 294260
CInjection molding-Mold temperature°CISO 29480

Processing recommendations
Drying temperature circulating air dryer°C -120
Drying time circulating air dryerh -4-8
Residual moisture content%Acc. to Karl Fischer 0.02
Melt temperature (Tmin - Tmax)°C -250-270
Mold temperature°C -80-100

Notes
1Typical properties: these are not to be construed as specifications
CThese property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Disclaimer
Disclaimer for commercial products
This information and our technical advice - whether verbal, in writing or by way of trials - are given in good faith but without warranty, and this also applies where proprietary rights of third parties are involved. Our advice does not release you from the obligation to verify the information currently provided - especially that contained in our safety data and technical information sheets - and to test our products as to their suitability for the intended processes and uses. The application, use and processing of our products and the products manufactured by you on the basis of our technical advice are beyond our control and, therefore, entirely your own responsibility. Our products are sold in accordance with the current version of our General Conditions of Sale and Delivery.
Test values
Unless specified to the contrary, the values given have been established on standardized test specimens at room temperature. The figures should be regarded as guide values only and not as binding minimum values. Kindly note that, under certain conditions, the properties can be affected to a considerable extent by the design of the mould/die, the processing conditions and the coloring.
Processing note
Under the recommended processing conditions small quantities of decomposition product may be given off during processing. To preclude any risk to the health and well-being of the machine operatives, tolerance limits for the work environment must be ensured by the provision of efficient exhaust ventilation and fresh air at the workplace in accordance with the Safety Data Sheet. In order to prevent the partial decomposition of the polymer and the generation of volatile decomposition products, the prescribed processing temperatures should not be substantially exceeded. Since excessively high temperatures are generally the result of operator error or defects in the heating system, special care and controls are essential in these areas.