Rheological properties |
C | Molding shrinkage, parallel | 60x60x2; 280 °C / MT 80 °C; 600 bar | % | ISO 294-4 | 0.3 | |
C | Molding shrinkage, transverse | 60x60x2; 280 °C / MT 80 °C; 600 bar | % | ISO 294-4 | 0.5 | |
| Post- shrinkage, parallel | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.05 | |
| Post- shrinkage, transverse | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.05 | |
Mechanical properties (23 °C/50 % r. h.) |
C | Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 20000 | 12500 |
C | Tensile Stress at break | 5 mm/min | MPa | ISO 527-1,-2 | 230 | 158 |
C | Tensile Strain at break | 5 mm/min | % | ISO 527-1,-2 | 2.5 | 3.5 |
C | Charpy impact strength | 23 °C | kJ/m² | ISO 179-1eU | 95 | 95 |
C | Charpy impact strength | -30 °C | kJ/m² | ISO 179-1eU | 95 | 95 |
C | Charpy notched impact strength | 23 °C | kJ/m² | ISO 179-1eA | 17 | 24 |
C | Charpy notched impact strength | -30 °C | kJ/m² | ISO 179-1eA | 17 | |
| Izod impact strength | 23 °C | kJ/m² | ISO 180-1U | 90 | 90 |
| Izod impact strength | -30 °C | kJ/m² | ISO 180-1U | 90 | 90 |
| Izod notched impact strength | 23 °C | kJ/m² | ISO 180-1A | 18 | 25 |
| Izod notched impact strength | -30 °C | kJ/m² | ISO 180-1A | 18 | |
| Flexural modulus | 2 mm/min | MPa | ISO 178-A | 20200 | 13500 |
| Flexural strength | 2 mm/min | MPa | ISO 178-A | 390 | 250 |
| Flexural strain at flexural strength | 2 mm/min | % | ISO 178-A | 3 | 4 |
| Flexural stress at 3.5 % strain | 2 mm/min | MPa | ISO 178-A | | 245 |
C | Puncture maximum force | 23 °C | N | ISO 6603-2 | 1300 | |
C | Puncture maximum force | -30 °C | N | ISO 6603-2 | 1200 | |
C | Puncture energy | 23 °C | J | ISO 6603-2 | 4.5 | |
C | Puncture energy | -30 °C | J | ISO 6603-2 | 3.8 | |
Thermal properties |
C | Melting temperature | 10 °C/min | °C | ISO 11357-1,-3 | 221 | |
C | Temperature of deflection under load | 1.80 MPa | °C | ISO 75-1,-2 | 213 | |
C | Temperature of deflection under load | 0.45 MPa | °C | ISO 75-1,-2 | 220 | |
C | Coefficient of linear thermal expansion, parallel | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.1 | |
C | Coefficient of linear thermal expansion, transverse | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.8 | |
| Resistance to heat (ball pressure test) | | °C | IEC 60695-10-2 | 210 | |
| Glow wire test (GWFI) | 0.75 mm | °C | IEC 60695-2-12 | 700 | |
| Glow wire test (GWFI) | 1.5 mm | °C | IEC 60695-2-12 | 725 | |
| Glow wire test (GWFI) | 3.0 mm | °C | IEC 60695-2-12 | 825 | |
| Glow wire test (GWIT) | 0.75 mm | °C | IEC 60695-2-13 | 725 | |
| Glow wire test (GWIT) | 1.5 mm | °C | IEC 60695-2-13 | 750 | |
| Glow wire test (GWIT) | 3.0 mm | °C | IEC 60695-2-13 | 750 | |
Electrical properties (23 °C/50 % r. h.) |
C | Relative permittivity | 100 Hz | - | IEC 60250 | 4.3 | 8.71 |
C | Relative permittivity | 1 MHz | - | IEC 60250 | 5.07 | 4.68 |
C | Dissipation factor | 100 Hz | 10-4 | IEC 60250 | 0.02 | 0.1 |
C | Dissipation factor | 1 MHz | 10-4 | IEC 60250 | 0.03 | 0.06 |
C | Volume resistivity | | Ohm·m | IEC 62631-3 | 6.14E+12 | 6.60E+10 |
C | Surface resistivity | | Ohm | IEC 62631-3 | 5.82E+14 | 2.64E+14 |
C | Electric strength | 1 mm | kV/mm | IEC 60243-1 | 28.6 | 25.8 |
C | Comparative tracking index CTI | Solution A | Rating | IEC 60112 | 600 | |
Other properties (23 °C) |
C | Density | | kg/m³ | ISO 1183 | 1710 | |
| Bulk density | | kg/m³ | ISO 60 | 750 | |
Processing conditions for test specimens |
C | Injection molding-Melt temperature | | °C | ISO 294 | 280 | |
C | Injection molding-Mold temperature | | °C | ISO 294 | 80 | |
Processing recommendations |
| Drying temperature dry air dryer | | °C | - | 80 | |
| Drying time dry air dryer | | h | - | 2-6 | |
| Residual moisture content | | % | Acc. to Karl Fischer | 0.05-0.15 | |
| Melt temperature (Tmin - Tmax) | | °C | - | 270-290 | |
| Mold temperature | | °C | - | 80-120 | |