Durethan T40 000000

  _More Info 
  _Data sheet ISO (PDF) 

 

Data sheet

PA 6I, non-reinforced, injection molding, extrusion
 
ISO/ ASTM
 
ISO Shortname:  ISO 16396-PA 6I,,GT,S12-030
PropertyTest ConditionUnitStandardguide value
 d.a.m.cond.
Rheological properties
Molding shrinkage, parallel150x105x3; 270 °C / WZ 80 °C; 500 bar%acc. ISO 25770.53
Molding shrinkage, transverse150x105x3; 270 °C / WZ 80 °C; 500 bar%acc. ISO 25770.49
Post- shrinkage, parallel150x105x3; 100 °C; 4 h%acc. ISO 25770.13
Post- shrinkage, transverse150x105x3; 100 °C; 4 h%acc. ISO 25770.09

Mechanical properties (23 °C/50 % r. h.)
CTensile modulus1 mm/minMPaISO 527-1,-233003000
CYield stress50 mm/minMPaISO 527-1,-211090
CYield strain50 mm/min%ISO 527-1,-26.05.0
CCharpy impact strength23 °CkJ/m²ISO 179-1eUNN
CCharpy impact strength-30 °CkJ/m²ISO 179-1eUNN
CCharpy notched impact strength23 °CkJ/m²ISO 179-1eA< 10< 10
CCharpy notched impact strength-30 °CkJ/m²ISO 179-1eA< 10< 10
Charpy notched impact strength-40 °CkJ/m²ISO 179-1eA< 10< 10
Izod notched impact strength-30 °CkJ/m²ISO 180-1A< 10< 10
Izod notched impact strength-40 °CkJ/m²ISO 180-1A< 10< 10
Flexural modulus2 mm/minMPaISO 178-A30003000
Flexural strength2 mm/minMPaISO 178-A150130
Flexural strain at flexural strength2 mm/min%ISO 178-A7.05.0
Flexural stress at 3.5 % strain2 mm/minMPaISO 178-A105110

Thermal properties
CTemperature of deflection under load1.80 MPa°CISO 75-1,-2105
CTemperature of deflection under load0.45 MPa°CISO 75-1,-2115
Vicat softening temperature50 N; 120 °C/h°CISO 306125
CCoefficient of linear thermal expansion, parallel23 to 55 °C10-4/KISO 11359-1,-20.7
CCoefficient of linear thermal expansion, transverse23 to 55 °C10-4/KISO 11359-1,-20.8
CBurning behavior UL 941.5 mmClassUL 94V-2
CBurning behavior UL 940.75 mmClassUL 94V-2
Glow wire test (GWFI)2.0 mm°CIEC 60695-2-12960
CVicat softening temperature50 N; 50 °C/h°CISO 306125

Electrical properties (23 °C/50 % r. h.)
CRelative permittivity100 Hz-IEC 602504.34.6
CRelative permittivity1 MHz-IEC 602503.84.0
CDissipation factor100 Hz10-4IEC 60250400480
CDissipation factor1 MHz10-4IEC 602509001100
CVolume resistivityOhm·mIEC 600931E131E13
CSurface resistivityOhmIEC 600931E151E15
CElectric strength1 mmkV/mmIEC 60243-12528
CComparative tracking index CTISolution ARatingIEC 60112600

Other properties (23 °C)
CWater absorption (Saturation value)Water at 23 °C%ISO 626.0
CWater absorption (Equilibrium value)23 °C; 50 % RH%ISO 622.0
CDensitykg/m³ISO 11831180

Processing conditions for test specimens
CInjection molding-Melt temperature°CISO 294270
CInjection molding-Mold temperature°CISO 29480

Processing recommendations
Drying temperature dry air dryer°C -80
Drying time dry air dryerh -2-6
Residual moisture content%Acc. to Karl Fischer 0.03-0.12
Melt temperature (Tmin - Tmax)°C -260-280
Mold temperature°C -80-100
CThese property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Disclaimer
Disclaimer for commercial products
This information and our technical advice - whether verbal, in writing or by way of trials - are given in good faith but without warranty, and this also applies where proprietary rights of third parties are involved. Our advice does not release you from the obligation to verify the information currently provided - especially that contained in our safety data and technical information sheets - and to test our products as to their suitability for the intended processes and uses. The application, use and processing of our products and the products manufactured by you on the basis of our technical advice are beyond our control and, therefore, entirely your own responsibility. Our products are sold in accordance with the current version of our General Conditions of Sale and Delivery.
Test values
Unless specified to the contrary, the values given have been established on standardized test specimens at room temperature. The figures should be regarded as guide values only and not as binding minimum values. Kindly note that, under certain conditions, the properties can be affected to a considerable extent by the design of the mould/die, the processing conditions and the coloring.
Processing note
Under the recommended processing conditions small quantities of decomposition product may be given off during processing. To preclude any risk to the health and well-being of the machine operatives, tolerance limits for the work environment must be ensured by the provision of efficient exhaust ventilation and fresh air at the workplace in accordance with the Safety Data Sheet. In order to prevent the partial decomposition of the polymer and the generation of volatile decomposition products, the prescribed processing temperatures should not be substantially exceeded. Since excessively high temperatures are generally the result of operator error or defects in the heating system, special care and controls are essential in these areas.
Conditioning
Conditioning in accordance with ISO 1110 (70 °C; 62 % r.h.)