Rheological properties |
C | Molding shrinkage, parallel | 60x60x2; 290 °C / MT 80 °C; 600 bar | % | ISO 294-4 | 0.3 | |
C | Molding shrinkage, transverse | 60x60x2; 290 °C / MT 80 °C; 600 bar | % | ISO 294-4 | 0.8 | |
| Post- shrinkage, parallel | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.02 | |
| Post- shrinkage, transverse | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.05 | |
Mechanical properties (23 °C/50 % r. h.) |
C | Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 12000 | 7400 |
C | Tensile Stress at break | 5 mm/min | MPa | ISO 527-1,-2 | 170 | 110 |
C | Tensile Strain at break | 5 mm/min | % | ISO 527-1,-2 | 2.5 | 4.5 |
C | Charpy impact strength | 23 °C | kJ/m² | ISO 179-1eU | 60 | 65 |
C | Charpy impact strength | -30 °C | kJ/m² | ISO 179-1eU | 60 | 55 |
C | Charpy notched impact strength | 23 °C | kJ/m² | ISO 179-1eA | <10 | 15 |
C | Charpy notched impact strength | -30 °C | kJ/m² | ISO 179-1eA | <10 | <10 |
| Izod impact strength | 23 °C | kJ/m² | ISO 180-1U | 55 | 65 |
| Izod impact strength | -30 °C | kJ/m² | ISO 180-1U | 55 | 50 |
| Izod notched impact strength | 23 °C | kJ/m² | ISO 180-1A | 10 | 15 |
| Izod notched impact strength | -30 °C | kJ/m² | ISO 180-1A | <10 | <10 |
| Flexural modulus | 2 mm/min | MPa | ISO 178-A | 11400 | 7000 |
| Flexural strength | 2 mm/min | MPa | ISO 178-A | 255 | 170 |
| Flexural strain at flexural strength | 2 mm/min | % | ISO 178-A | 3 | 4.5 |
| Flexural stress at 3.5 % strain | 2 mm/min | MPa | ISO 178-A | | 160 |
C | Puncture maximum force | 23 °C | N | ISO 6603-2 | 840 | |
C | Puncture maximum force | -30 °C | N | ISO 6603-2 | 700 | |
C | Puncture energy | 23 °C | J | ISO 6603-2 | 3.1 | |
C | Puncture energy | -30 °C | J | ISO 6603-2 | 2.3 | |
Thermal properties |
C | Melting temperature | 10 °C/min | °C | ISO 11357-1,-3 | 261 | |
C | Temperature of deflection under load | 1.80 MPa | °C | ISO 75-1,-2 | 240 | |
C | Temperature of deflection under load | 0.45 MPa | °C | ISO 75-1,-2 | 250 | |
C | Coefficient of linear thermal expansion, parallel | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.1 | |
C | Coefficient of linear thermal expansion, transverse | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 1 | |
Electrical properties (23 °C/50 % r. h.) |
C | Volume resistivity | | Ohm·m | IEC 62631-3 | 1E+03 | |
| Surface resistivity | | Ohm | IEC 60167 | 1E+04 | |
Other properties (23 °C) |
C | Water absorption (Saturation value) | Water at 23 °C | % | ISO 62 | 5 | |
C | Water absorption (Equilibrium value) | 23 °C; 50 % RH | % | ISO 62 | 1.7 | |
C | Density | | kg/m³ | ISO 1183 | 1300 | |
| Bulk density | | kg/m³ | ISO 60 | 700 | |
Processing conditions for test specimens |
C | Injection molding-Melt temperature | | °C | ISO 294 | 290 | |
C | Injection molding-Mold temperature | | °C | ISO 294 | 80 | |
Processing recommendations |
| Drying temperature dry air dryer | | °C | - | 80 | |
| Drying time dry air dryer | | h | - | 2-6 | |
| Residual moisture content | | % | Acc. to Karl Fischer | 0.03-0.07 | |
| Melt temperature (Tmin - Tmax) | | °C | - | 280-300 | |
| Mold temperature | | °C | - | 80-120 | |