Pocan B7425 000000

  _More Info 
  _Data sheet ISO (PDF) 

 

Data sheet

PBT, 20% micro glass beads, injection molding, low tendency to warp, improved surface finish
 
ISO Shortname:  ISO 20028-PBT,GB20,GHMR,11-030
PropertyTest ConditionUnitStandardguide value1
Rheological properties
CMelt volume-flow rate260 °C; 5 kgcm³/(10 min)ISO 1133-135
CMolding shrinkage, parallel60x60x2; 260 °C / MT 80 °C; 600 bar%ISO 294-42.1
CMolding shrinkage, transverse60x60x2; 260 °C / MT 80 °C; 600 bar%ISO 294-42.1
Post- shrinkage, parallel60x60x2; 120 °C; 4 h%ISO 294-40.2
Post- shrinkage, transverse60x60x2; 120 °C; 4 h%ISO 294-40.2

Mechanical properties (23 °C/50 % r. h.)
CTensile modulus1 mm/minMPaISO 527-1,-23300
CTensile Stress at break5 mm/minMPaISO 527-1,-250
CTensile Strain at break5 mm/min%ISO 527-1,-26.0
CTensile creep modulus1 hMPaISO 899-13300
CTensile creep modulus1000 hMPaISO 899-12700
CCharpy impact strength23 °CkJ/m²ISO 179-1eU35
CCharpy impact strength-30 °CkJ/m²ISO 179-1eU25
CCharpy notched impact strength23 °CkJ/m²ISO 179-1eA< 10
CCharpy notched impact strength-30 °CkJ/m²ISO 179-1eA< 10
Izod impact strength23 °CkJ/m²ISO 180-1U30
Izod impact strength-30 °CkJ/m²ISO 180-1U20
Izod notched impact strength23 °CkJ/m²ISO 180-1A< 10
Izod notched impact strength-30 °CkJ/m²ISO 180-1A< 10
Flexural modulus2 mm/minMPaISO 178-A3300
Flexural strength2 mm/minMPaISO 178-A90
Flexural strain at flexural strength2 mm/min%ISO 178-A5.0
Flexural stress at 3.5 % strain2 mm/minMPaISO 178-A85
Ball indentation hardnessN/mm²ISO 2039-1160

Thermal properties
CMelting temperature10 °C/min°CISO 11357-1,-3225
CTemperature of deflection under load1.80 MPa°CISO 75-1,-270
CTemperature of deflection under load0.45 MPa°CISO 75-1,-2170
Vicat softening temperature50 N; 120 °C/h°CISO 306190
CCoefficient of linear thermal expansion, parallel23 to 55 °C10-4/KISO 11359-1,-21.0
CCoefficient of linear thermal expansion, transverse23 to 55 °C10-4/KISO 11359-1,-21.0
CBurning behavior UL 941.5 mmClassUL 94HB
CBurning behavior UL 940.75 mmClassUL 94HB
COxygen indexMethod A%ISO 4589-223
Thermal conductivity23 °CW/(m·K)ISO 83020.28
Resistance to heat (ball pressure test)°CIEC 60695-10-2200
Temperature index (Tensile strength)20000 h°CIEC 60216-1140
Halving interval (Tensile strength)°CIEC 60216-114
Relative temperature index (Tensile strength)°CUL 746B130
Temperature index (Tensile impact strength)20000 h°CIEC 60216-1130
Halving interval (Tensile impact strength)°CIEC 60216-17.8
Relative temperature index (Tensile impact strength)°CUL 746B125
Temperature index (Electric strength)20000 h°CIEC 60216-1160
Halving interval (Electric strength)°CIEC 60216-111.4
Relative temperature index (Electric strength)°CUL 746B130
Glow wire test (GWFI)2.0 mm°CIEC 60695-2-12650
Burning behavior US-FMVSS302 ISO 3795passed

Electrical properties (23 °C/50 % r. h.)
CRelative permittivity100 Hz-IEC 602503.8
CRelative permittivity1 MHz-IEC 602503.6
CDissipation factor1 MHz10-4IEC 60250170
CVolume resistivityOhm·mIEC 62631-3>1E13
CSurface resistivityOhmIEC 62631-3>1E15
CElectric strength1 mmkV/mmIEC 60243-125
CComparative tracking index CTISolution ARatingIEC 60112250

Other properties (23 °C)
CWater absorption (Saturation value)Water at 23 °C%ISO 620.4
CWater absorption (Equilibrium value)23 °C; 50 % RH%ISO 620.1
CDensitykg/m³ISO 11831440
Bulk densitykg/m³ISO 60900

Material specific properties
CViscosity numbercm³/gISO 1628-5130

Processing conditions for test specimens
CInjection molding-Melt temperature°CISO 294260
CInjection molding-Mold temperature°CISO 29480

Processing recommendations
Drying temperature circulating air dryer°C -120
Drying time circulating air dryerh -4-8
Residual moisture content%Acc. to Karl Fischer 0.00-0.02
Melt temperature (Tmin - Tmax)°C -250-270
Mold temperature°C -80-100

Notes
1Typical properties: these are not to be construed as specifications
CThese property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Disclaimer
Disclaimer for commercial products
This information and our technical advice - whether verbal, in writing or by way of trials - are given in good faith but without warranty, and this also applies where proprietary rights of third parties are involved. Our advice does not release you from the obligation to verify the information currently provided - especially that contained in our safety data and technical information sheets - and to test our products as to their suitability for the intended processes and uses. The application, use and processing of our products and the products manufactured by you on the basis of our technical advice are beyond our control and, therefore, entirely your own responsibility. Our products are sold in accordance with the current version of our General Conditions of Sale and Delivery.
Test values
Unless specified to the contrary, the values given have been established on standardized test specimens at room temperature. The figures should be regarded as guide values only and not as binding minimum values. Kindly note that, under certain conditions, the properties can be affected to a considerable extent by the design of the mould/die, the processing conditions and the coloring.
Processing note
Under the recommended processing conditions small quantities of decomposition product may be given off during processing. To preclude any risk to the health and well-being of the machine operatives, tolerance limits for the work environment must be ensured by the provision of efficient exhaust ventilation and fresh air at the workplace in accordance with the Safety Data Sheet. In order to prevent the partial decomposition of the polymer and the generation of volatile decomposition products, the prescribed processing temperatures should not be substantially exceeded. Since excessively high temperatures are generally the result of operator error or defects in the heating system, special care and controls are essential in these areas.