Pocan BFN2502 000000

  _More Info 
  _Data sheet ISO (PDF) 

 

Data sheet

PBT, non-reinforced, injection molding, halogen free flame retardant
 
ISO Shortname:  ISO 20028-PBT,,GFHMR,11-030; ISO 1043-4 FR(30+40)
PropertyTest ConditionUnitStandardguide value
Rheological properties
CMelt volume-flow rate260 °C; 2.16 kgcm³/(10 min)ISO 1133-120
CMolding shrinkage, parallel60x60x2%ISO 294-42.3
CMolding shrinkage, transverse60x60x2%ISO 294-42.2
Post- shrinkage, parallel60x60x2%ISO 294-40.2
Post- shrinkage, transverse60x60x2%ISO 294-40.2

Mechanical properties (23 °C/50 % r. h.)
CTensile modulus1 mm/minMPaISO 527-1,-22900
CYield stress50 mm/minMPaISO 527-1,-240
CYield strain50 mm/min%ISO 527-1,-22.6
CNominal strain at break50 mm/min%ISO 527-1,-25.5
CCharpy impact strength23 °CkJ/m²ISO 179-1eU22
CCharpy impact strength-30 °CkJ/m²ISO 179-1eU22
CCharpy notched impact strength23 °CkJ/m²ISO 179-1eA<10
CCharpy notched impact strength-30 °CkJ/m²ISO 179-1eA<10
Izod impact strength23 °CkJ/m²ISO 180-1U18
Izod impact strength-30 °CkJ/m²ISO 180-1U18
Flexural modulus2 mm/minMPaISO 178-A3000
Flexural strength2 mm/minMPaISO 178-A75
Flexural strain at flexural strength2 mm/min%ISO 178-A5.2
Flexural stress at 3.5 % strain2 mm/minMPaISO 178-A70

Thermal properties
CMelting temperature10 °C/min°CISO 11357-1,-3220
CTemperature of deflection under load1.80 MPa°CISO 75-1,-273
CTemperature of deflection under load0.45 MPa°CISO 75-1,-2166
CCoefficient of linear thermal expansion, parallel23 to 55 °C10-4/KISO 11359-1,-21
CCoefficient of linear thermal expansion, transverse23 to 55 °C10-4/KISO 11359-1,-21.1
CBurning behavior UL 940.4 mmClassUL 94V-0
Burning behavior UL 940.75 mmClassUL 94V-0
Burning behavior UL 941.5 mmClassUL 94V-0
Burning behavior UL 943.0 mmClassUL 94V-0
CBurning behavior UL 94-5V3.0 mmClassUL 945VA
COxygen indexMethod A%ISO 4589-236
Resistance to heat (ball pressure test)°CIEC 60695-10-2195
Glow wire test (GWFI)0.4 mm°CIEC 60695-2-12960
Glow wire test (GWFI)0.75 mm°CIEC 60695-2-12960
Glow wire test (GWFI)1.5 mm°CIEC 60695-2-12960
Glow wire test (GWFI)3.0 mm°CIEC 60695-2-12960
Glow wire test (GWIT)0.4 mm°CIEC 60695-2-13750
Glow wire test (GWIT)0.75 mm°CIEC 60695-2-13725
Glow wire test (GWIT)1.5 mm°CIEC 60695-2-13725
Glow wire test (GWIT)3.0 mm°CIEC 60695-2-13725
CVicat softening temperature50 N; 50 °C/h°CISO 306215

Electrical properties (23 °C/50 % r. h.)
CRelative permittivity100 Hz-IEC 602503.4
CRelative permittivity1 MHz-IEC 602503.3
CDissipation factor100 Hz10-4IEC 6025069
CDissipation factor1 MHz10-4IEC 6025059
CVolume resistivityOhm·mIEC 600931.8E13
CSurface resistivityOhmIEC 600935.6E16
CElectric strength1 mmkV/mmIEC 60243-131
CComparative tracking index CTISolution ARatingIEC 60112600
Comparative tracking index CTISolution APLCUL 746A0

Other properties (23 °C)
CDensitykg/m³ISO 11831330
Bulk densitykg/m³ISO 60800

Processing conditions for test specimens
CInjection molding-Melt temperature°CISO 294260
CInjection molding-Mold temperature°CISO 29480

Processing recommendations
Drying temperature circulating air dryer°C -120
Drying time circulating air dryerh -4
Residual moisture content%Acc. to Karl Fischer 0.00-0.02
Melt temperature (Tmin - Tmax)°C -250-270
admissible residence time at Tmaxmin -<5
Mold temperature°C -70-90
CThese property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Disclaimer
Disclaimer for commercial products
This information and our technical advice - whether verbal, in writing or by way of trials - are given in good faith but without warranty, and this also applies where proprietary rights of third parties are involved. Our advice does not release you from the obligation to verify the information currently provided - especially that contained in our safety data and technical information sheets - and to test our products as to their suitability for the intended processes and uses. The application, use and processing of our products and the products manufactured by you on the basis of our technical advice are beyond our control and, therefore, entirely your own responsibility. Our products are sold in accordance with the current version of our General Conditions of Sale and Delivery.
Test values
Unless specified to the contrary, the values given have been established on standardized test specimens at room temperature. The figures should be regarded as guide values only and not as binding minimum values. Kindly note that, under certain conditions, the properties can be affected to a considerable extent by the design of the mould/die, the processing conditions and the coloring.
Processing note
Under the recommended processing conditions small quantities of decomposition product may be given off during processing. To preclude any risk to the health and well-being of the machine operatives, tolerance limits for the work environment must be ensured by the provision of efficient exhaust ventilation and fresh air at the workplace in accordance with the Safety Data Sheet. In order to prevent the partial decomposition of the polymer and the generation of volatile decomposition products, the prescribed processing temperatures should not be substantially exceeded. Since excessively high temperatures are generally the result of operator error or defects in the heating system, special care and controls are essential in these areas.
LANXESS DEUTSCHLAND GMBH | D-50569 COLOGNE
Date: 21.11.2018