Pocan T7245 000000

  _More Info 
  _Data sheet ISO (PDF) 


Data sheet

PET, 45% glass fibers/mineral, injection molding, improved light reflection
ISO Shortname:  ISO 20028-PET,(GF+MD)45,GHMR,07-120
PropertyTest ConditionUnitStandardguide value1
Rheological properties
CMelt volume-flow rate270 °C; 5 kgcm³/(10 min)ISO 1133-135
CMolding shrinkage, parallel60x60x2; 270 °C / WZ 120 °C; 600 bar%ISO 294-40.4
CMolding shrinkage, transverse60x60x2; 270 °C / WZ 120 °C; 600 bar%ISO 294-41.0
Post- shrinkage, parallel60x60x2; 120 °C; 4 h%ISO 294-40.1
Post- shrinkage, transverse60x60x2; 120 °C; 4 h%ISO 294-40.1

Mechanical properties (23 °C/50 % r. h.)
CTensile modulus1 mm/minMPaISO 527-1,-212000
CTensile Stress at break5 mm/minMPaISO 527-1,-2115
CTensile Strain at break5 mm/min%ISO 527-1,-21.6
CCharpy impact strength23 °CkJ/m²ISO 179-1eU30
Izod impact strength23 °CkJ/m²ISO 180-1U30
Flexural modulus2 mm/minMPaISO 178-A11000
Flexural strength2 mm/minMPaISO 178-A170
Flexural strain at flexural strength2 mm/min%ISO 178-A2.0

Thermal properties
CMelting temperature10 °C/min°CISO 11357-1,-3260
CTemperature of deflection under load1.80 MPa°CISO 75-1,-2180
CTemperature of deflection under load0.45 MPa°CISO 75-1,-2230
CVicat softening temperature50 N; 50 °C/h°CISO 306220

Electrical properties (23 °C/50 % r. h.)
CComparative tracking index CTISolution ARatingIEC 60112225

Other properties (23 °C)
CDensitykg/m³ISO 11831825

Processing conditions for test specimens
CInjection molding-Melt temperature°CISO 294270
CInjection molding-Mold temperature°CISO 294120

Processing recommendations
Drying temperature circulating air dryer°C -120
Drying time circulating air dryerh -4-8
Residual moisture content%Acc. to Karl Fischer 0.00-0.02
Melt temperature (Tmin - Tmax)°C -260-290
Mold temperature°C -110-130

1Typical properties: these are not to be construed as specifications
CThese property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Disclaimer for commercial products
This information and our technical advice - whether verbal, in writing or by way of trials - are given in good faith but without warranty, and this also applies where proprietary rights of third parties are involved. Our advice does not release you from the obligation to verify the information currently provided - especially that contained in our safety data and technical information sheets - and to test our products as to their suitability for the intended processes and uses. The application, use and processing of our products and the products manufactured by you on the basis of our technical advice are beyond our control and, therefore, entirely your own responsibility. Our products are sold in accordance with the current version of our General Conditions of Sale and Delivery.
Test values
Unless specified to the contrary, the values given have been established on standardized test specimens at room temperature. The figures should be regarded as guide values only and not as binding minimum values. Kindly note that, under certain conditions, the properties can be affected to a considerable extent by the design of the mould/die, the processing conditions and the coloring.
Processing note
Under the recommended processing conditions small quantities of decomposition product may be given off during processing. To preclude any risk to the health and well-being of the machine operatives, tolerance limits for the work environment must be ensured by the provision of efficient exhaust ventilation and fresh air at the workplace in accordance with the Safety Data Sheet. In order to prevent the partial decomposition of the polymer and the generation of volatile decomposition products, the prescribed processing temperatures should not be substantially exceeded. Since excessively high temperatures are generally the result of operator error or defects in the heating system, special care and controls are essential in these areas.
LANXESS Performance Materials GmbH | DE 50569 COLOGNE | Germany