Durethan BKV15H3.0 000000 DUS008
  _More Info 
  _Data sheet ISO (PDF) 

 

Data sheet
PA 6, 15 % glass fibers, injection molding, heat-aging stabilized
 
ISO Shortname:  ISO 16396-PA 6,GF15,GHR,S14-070
PropertyTest ConditionUnitStandardguide value1
 d.a.m.cond.
Rheological properties
Molding shrinkage, parallel150x105x3; 280 °C / MT 80 °C; 500 bar%acc. ISO 25770.35
Molding shrinkage, transverse150x105x3; 280 °C / MT 80 °C; 500 bar%acc. ISO 25770.60
Post- shrinkage, parallel150x105x3; 120 °C; 4 h%acc. ISO 25770.15
Post- shrinkage, transverse150x105x3; 120 °C; 4 h%acc. ISO 25770.15

Mechanical properties (23 °C/50 % r. h.)
CTensile modulus1 mm/minMPaISO 527-1,-265003100
CTensile Stress at break5 mm/minMPaISO 527-1,-213065
CTensile Strain at break5 mm/min%ISO 527-1,-2312
CCharpy impact strength23 °CkJ/m²ISO 179-1eU50100
CCharpy impact strength-30 °CkJ/m²ISO 179-1eU4545
Izod impact strength23 °CkJ/m²ISO 180-1U4585
Izod impact strength-30 °CkJ/m²ISO 180-1U4040
Izod notched impact strength23 °CkJ/m²ISO 180-1A<1010
Flexural modulus2 mm/minMPaISO 178-A55003100
Flexural strength2 mm/minMPaISO 178-A205110
Flexural strain at flexural strength2 mm/min%ISO 178-A5.38
Flexural stress at 3.5 % strain2 mm/minMPaISO 178-A18080

Thermal properties
CMelting temperature10 °C/min°CISO 11357-1,-3220
CTemperature of deflection under load1.80 MPa°CISO 75-1,-2195
CTemperature of deflection under load0.45 MPa°CISO 75-1,-2215
CCoefficient of linear thermal expansion, parallel23 to 55 °C10-4/KISO 11359-1,-20.3
CCoefficient of linear thermal expansion, transverse23 to 55 °C10-4/KISO 11359-1,-21
CBurning behavior UL 94ClassUL 94HB

Electrical properties (23 °C/50 % r. h.)
CVolume resistivityOhm·mIEC 600932.61E+15
CSurface resistivityOhmIEC 600938.15E+13
CComparative tracking index CTISolution ARatingIEC 60112550

Other properties (23 °C)
CDensitykg/m³ISO 11831228

Processing conditions for test specimens
CInjection molding-Melt temperature°CISO 294280
CInjection molding-Mold temperature°CISO 29480

Processing recommendations
Drying temperature dry air dryer°C -80
Drying time dry air dryerh -2-6
Residual moisture content%Acc. to Karl Fischer 0.03-0.12
Melt temperature (Tmin - Tmax)°C -260-290
Mold temperature°C -80-100

Notes
1Typical properties: these are not to be construed as specifications
CThese property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Disclaimer
Disclaimer for commercial products
This information and our technical advice - whether verbal, in writing or by way of trials - are given in good faith but without warranty, and this also applies where proprietary rights of third parties are involved. Our advice does not release you from the obligation to verify the information currently provided - especially that contained in our safety data and technical information sheets - and to test our products as to their suitability for the intended processes and uses. The application, use and processing of our products and the products manufactured by you on the basis of our technical advice are beyond our control and, therefore, entirely your own responsibility. Our products are sold in accordance with the current version of our General Conditions of Sale and Delivery.
Test values
Unless specified to the contrary, the values given have been established on standardized test specimens at room temperature. The figures should be regarded as guide values only and not as binding minimum values. Kindly note that, under certain conditions, the properties can be affected to a considerable extent by the design of the mould/die, the processing conditions and the coloring.
Processing note
Under the recommended processing conditions small quantities of decomposition product may be given off during processing. To preclude any risk to the health and well-being of the machine operatives, tolerance limits for the work environment must be ensured by the provision of efficient exhaust ventilation and fresh air at the workplace in accordance with the Safety Data Sheet. In order to prevent the partial decomposition of the polymer and the generation of volatile decomposition products, the prescribed processing temperatures should not be substantially exceeded. Since excessively high temperatures are generally the result of operator error or defects in the heating system, special care and controls are essential in these areas.
Conditioning
Conditioning in accordance with ISO 1110 (70 °C; 62 % r.h.)
LANXESS Performance Materials GmbH | DE 50569 COLOGNE | Germany
Date: 01.03.2022