Rheological properties |
C | Molding shrinkage, parallel | 60x60x2 | % | ISO 294-4 | 0.15 | |
C | Molding shrinkage, transverse | 60x60x2 | % | ISO 294-4 | 0.65 | |
| Post- shrinkage, parallel | 60x60x2 | % | ISO 294-4 | 0.1 | |
| Post- shrinkage, transverse | 60x60x2 | % | ISO 294-4 | 0.1 | |
Mechanical properties (23 °C/50 % r. h.) |
C | Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 12500 | 7700 |
C | Tensile Stress at break | 5 mm/min | MPa | ISO 527-1,-2 | 190 | 115 |
C | Tensile Strain at break | 5 mm/min | % | ISO 527-1,-2 | 3.0 | 5.5 |
C | Charpy impact strength | 23 °C | kJ/m² | ISO 179-1eU | 85 | 90 |
C | Charpy impact strength | -30 °C | kJ/m² | ISO 179-1eU | 70 | 70 |
C | Charpy notched impact strength | 23 °C | kJ/m² | ISO 179-1eA | 15 | 25 |
C | Charpy notched impact strength | -30 °C | kJ/m² | ISO 179-1eA | 10 | 10 |
| Izod impact strength | 23 °C | kJ/m² | ISO 180-1U | 80 | 85 |
| Izod impact strength | -30 °C | kJ/m² | ISO 180-1U | 70 | |
| Izod notched impact strength | 23 °C | kJ/m² | ISO 180-1A | 15 | 23 |
| Izod notched impact strength | -30 °C | kJ/m² | ISO 180-1A | 10 | |
| Flexural modulus | 2 mm/min | MPa | ISO 178-A | 11500 | 7700 |
| Flexural strength | 2 mm/min | MPa | ISO 178-A | 285 | 190 |
| Flexural strain at flexural strength | 2 mm/min | % | ISO 178-A | 3.2 | 4.8 |
| Flexural stress at 3.5 % strain | 2 mm/min | MPa | ISO 178-A | | 170 |
C | Puncture maximum force | 23 °C | N | ISO 6603-2 | 900 | |
C | Puncture maximum force | -30 °C | N | ISO 6603-2 | 800 | |
C | Puncture energy | 23 °C | J | ISO 6603-2 | 3.2 | |
C | Puncture energy | -30 °C | J | ISO 6603-2 | 3.4 | |
Thermal properties |
C | Melting temperature | 10 °C/min | °C | ISO 11357-1,-3 | 220 | |
C | Temperature of deflection under load | 1.80 MPa | °C | ISO 75-1,-2 | 208 | |
C | Temperature of deflection under load | 0.45 MPa | °C | ISO 75-1,-2 | 220 | |
| Vicat softening temperature | 50 N; 120 °C/h | °C | ISO 306 | 210 | |
Other properties (23 °C) |
C | Water absorption (Saturation value) | Water at 23 °C | % | ISO 62 | 5.8 | |
C | Water absorption (Equilibrium value) | 23 °C; 50 % RH | % | ISO 62 | 1.7 | |
C | Density | | kg/m³ | ISO 1183 | 1450 | |
| Bulk density | | kg/m³ | ISO 60 | 700 | |
Processing conditions for test specimens |
C | Injection molding-Melt temperature | | °C | ISO 294 | 280 | |
C | Injection molding-Mold temperature | | °C | ISO 294 | 80 | |
Processing recommendations |
| Drying temperature dry air dryer | | °C | - | 80 | |
| Drying time dry air dryer | | h | - | 2-6 | |
| Melt temperature (Tmin - Tmax) | | °C | - | 260-290 | |
| Mold temperature | | °C | - | 80-100 | |