Rheological properties |
C | Molding shrinkage, parallel | 60x60x2; 600 bar | % | ISO 294-4 | 0.9 | |
C | Molding shrinkage, transverse | 60x60x2; 600 bar | % | ISO 294-4 | 0.9 | |
| Post- shrinkage, parallel | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.1 | |
| Post- shrinkage, transverse | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.1 | |
Mechanical properties (23 °C/50 % r. h.) |
C | Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 12800 | 6100 |
C | Tensile Stress at break | 5 mm/min | MPa | ISO 527-1,-2 | 90 | 55 |
C | Tensile Strain at break | 5 mm/min | % | ISO 527-1,-2 | 1.1 | 1.8 |
C | Charpy impact strength | 23 °C | kJ/m² | ISO 179-1eU | 25 | 25 |
C | Charpy impact strength | -30 °C | kJ/m² | ISO 179-1eU | 15 | 10 |
C | Charpy notched impact strength | 23 °C | kJ/m² | ISO 179-1eA | <10 | <10 |
C | Charpy notched impact strength | -30 °C | kJ/m² | ISO 179-1eA | <10 | <10 |
| Izod impact strength | 23 °C | kJ/m² | ISO 180-1U | 25 | 20 |
| Izod impact strength | -30 °C | kJ/m² | ISO 180-1U | 17 | 10 |
| Izod notched impact strength | 23 °C | kJ/m² | ISO 180-1A | <10 | <10 |
| Izod notched impact strength | -30 °C | kJ/m² | ISO 180-1A | <10 | <10 |
| Flexural modulus | 2 mm/min | MPa | ISO 178-A | 13600 | 6700 |
| Flexural strength | 2 mm/min | MPa | ISO 178-A | 165 | 90 |
| Flexural strain at flexural strength | 2 mm/min | % | ISO 178-A | 2 | 2.1 |
| Ball indentation hardness | | N/mm² | ISO 2039-1 | 340 | |
Thermal properties |
C | Melting temperature | 10 °C/min | °C | ISO 11357-1,-3 | 220 | |
C | Temperature of deflection under load | 1.80 MPa | °C | ISO 75-1,-2 | 145 | |
C | Temperature of deflection under load | 0.45 MPa | °C | ISO 75-1,-2 | 195 | |
| Vicat softening temperature | 50 N; 120 °C/h | °C | ISO 306 | 210 | |
C | Coefficient of linear thermal expansion, parallel | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.4 | |
C | Coefficient of linear thermal expansion, transverse | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.4 | |
| Thermal conductivity, in-plane | | W/(m·K) | ISO 22007-4 | 1.7 | |
| Thermal conductivity, through-plane | | W/(m·K) | ISO 22007-4 | 1.2 | |
| Burning behavior UL 94 | 1.5 mm | Class | UL 94 | V-0 | |
| Resistance to heat (ball pressure test) | | °C | IEC 60695-10-2 | 200 | |
| Glow wire test (GWFI) | 0.75 mm | °C | IEC 60695-2-12 | 960 | |
| Glow wire test (GWFI) | 1.5 mm | °C | IEC 60695-2-12 | 960 | |
| Glow wire test (GWFI) | 3.0 mm | °C | IEC 60695-2-12 | 960 | |
| Glow wire test (GWIT) | 0.75 mm | °C | IEC 60695-2-13 | 775 | |
| Glow wire test (GWIT) | 1.5 mm | °C | IEC 60695-2-13 | 775 | |
| Glow wire test (GWIT) | 3.0 mm | °C | IEC 60695-2-13 | 800 | |
Electrical properties (23 °C/50 % r. h.) |
C | Volume resistivity | | Ohm·m | IEC 62631-3 | 3.4E13 | |
C | Surface resistivity | | Ohm | IEC 62631-3 | 7.2E14 | |
C | Electric strength | 1 mm | kV/mm | IEC 60243-1 | 30 | |
C | Comparative tracking index CTI | Solution A | Rating | IEC 60112 | 600 | |
| Comparative tracking index CTI | Solution A | PLC | UL 746A | 0 | |
Other properties (23 °C) |
C | Water absorption (Saturation value) | Water at 23 °C | % | ISO 62 | 2.7 | |
C | Water absorption (Equilibrium value) | 23 °C; 50 % RH | % | ISO 62 | 0.9 | |
C | Density | | kg/m³ | ISO 1183 | 1925 | |
| Bulk density | | kg/m³ | ISO 60 | 700 | |
Processing conditions for test specimens |
C | Injection molding-Melt temperature | | °C | ISO 294 | 280 | |
C | Injection molding-Mold temperature | | °C | ISO 294 | 80 | |
Processing recommendations |
| Drying temperature dry air dryer | | °C | - | 80 | |
| Drying time dry air dryer | | h | - | 2-6 | |
| Residual moisture content | | % | Acc. to Karl Fischer | 0.03-0.12 | |
| Melt temperature (Tmin - Tmax) | | °C | - | 260-300 | |
| Mold temperature | | °C | - | 80-100 | |