Durethan BTC965FM30 000000

  _More Info 
  _Data sheet ISO (PDF) 

 

Data sheet

PA 6, 68 % mineral, injection molding, halogen free flame retardant, improved heat conductivity, heat-aging stabilized
 
ISO Shortname:  ISO 16396-PA 6,MD68 FR(61),GF2HR,S12-140
PropertyTest ConditionUnitStandardguide value
 d.a.m.cond.
Rheological properties
CMolding shrinkage, parallel60x60x2; 260 °C / MT 80 °C; 600 bar%ISO 294-40.6
CMolding shrinkage, transverse60x60x2; 260 °C / MT 80 °C; 600 bar%ISO 294-40.5
Post- shrinkage, parallel60x60x2; 120 °C; 4 h%ISO 294-40.1
Post- shrinkage, transverse60x60x2; 120 °C; 4 h%ISO 294-40.1

Mechanical properties (23 °C/50 % r. h.)
CTensile modulus1 mm/minMPaISO 527-1,-2131006700
CTensile Stress at break5 mm/minMPaISO 527-1,-27545
CTensile Strain at break5 mm/min%ISO 527-1,-20.71.2
CCharpy impact strength23 °CkJ/m²ISO 179-1eU99
Izod impact strength23 °CkJ/m²ISO 180-1U1010
Flexural modulus2 mm/minMPaISO 178-A142006200
Flexural strength2 mm/minMPaISO 178-A13065
Flexural strain at flexural strength2 mm/min%ISO 178-A1.21.8

Thermal properties
CMelting temperature10 °C/min°CISO 11357-1,-3220
CTemperature of deflection under load1.80 MPa°CISO 75-1,-2160
Vicat softening temperature50 N; 120 °C/h°CISO 306212
CCoefficient of linear thermal expansion, parallel23 to 55 °C10-4/KISO 11359-1,-20.4
CCoefficient of linear thermal expansion, transverse23 to 55 °C10-4/KISO 11359-1,-20.5
Thermal conductivity, in-planeW/(m·K)ISO 22007-42.5
Thermal conductivity, through-planeW/(m·K)ISO 22007-41.3
CBurning behavior UL 941.5 mmClassUL 94V-0
CBurning behavior UL 940.75 mmClassUL 94V-0
CBurning behavior UL 94-5V1.5 mmClassUL 945VA
COxygen indexMethod A%ISO 4589-2>100
Glow wire test (GWFI)0.75 mm°CIEC 60695-2-12960
Glow wire test (GWFI)1.5 mm°CIEC 60695-2-12960
Glow wire test (GWFI)3.0 mm°CIEC 60695-2-12960
Glow wire test (GWIT)0.75 mm°CIEC 60695-2-13750
Glow wire test (GWIT)1.5 mm°CIEC 60695-2-13750
Glow wire test (GWIT)3.0 mm°CIEC 60695-2-13800

Electrical properties (23 °C/50 % r. h.)
CRelative permittivity100 Hz-IEC 602504.8
CRelative permittivity1 MHz-IEC 602504.4
CDissipation factor100 Hz10-4IEC 60250170
CDissipation factor1 MHz10-4IEC 60250140
CVolume resistivityOhm·mIEC 600935.30E+13
CSurface resistivityOhmIEC 600933.8E+15
CElectric strength1 mmkV/mmIEC 60243-134
CComparative tracking index CTISolution ARatingIEC 60112600
Comparative tracking index CTISolution APLCUL 746A0

Other properties (23 °C)
CWater absorption (Saturation value)Water at 23 °C%ISO 623.2
CWater absorption (Equilibrium value)23 °C; 50 % RH%ISO 621
CDensitykg/m³ISO 11831730
Bulk densitykg/m³ISO 60800

Processing conditions for test specimens
CInjection molding-Melt temperature°CISO 294280
CInjection molding-Mold temperature°CISO 29480

Processing recommendations
Drying temperature dry air dryer°C -80
Drying time dry air dryerh -2-6
Residual moisture content%Acc. to Karl Fischer 0.03-0.12
Melt temperature (Tmin - Tmax)°C -260-290
Mold temperature°C -80-100
CThese property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Disclaimer
Disclaimer for commercial products
This information and our technical advice - whether verbal, in writing or by way of trials - are given in good faith but without warranty, and this also applies where proprietary rights of third parties are involved. Our advice does not release you from the obligation to verify the information currently provided - especially that contained in our safety data and technical information sheets - and to test our products as to their suitability for the intended processes and uses. The application, use and processing of our products and the products manufactured by you on the basis of our technical advice are beyond our control and, therefore, entirely your own responsibility. Our products are sold in accordance with the current version of our General Conditions of Sale and Delivery.
Test values
Unless specified to the contrary, the values given have been established on standardized test specimens at room temperature. The figures should be regarded as guide values only and not as binding minimum values. Kindly note that, under certain conditions, the properties can be affected to a considerable extent by the design of the mould/die, the processing conditions and the coloring.
Processing note
Under the recommended processing conditions small quantities of decomposition product may be given off during processing. To preclude any risk to the health and well-being of the machine operatives, tolerance limits for the work environment must be ensured by the provision of efficient exhaust ventilation and fresh air at the workplace in accordance with the Safety Data Sheet. In order to prevent the partial decomposition of the polymer and the generation of volatile decomposition products, the prescribed processing temperatures should not be substantially exceeded. Since excessively high temperatures are generally the result of operator error or defects in the heating system, special care and controls are essential in these areas.
Conditioning
Conditioning in accordance with ISO 1110 (70 °C; 62 % r.h.)
LANXESS DEUTSCHLAND GMBH | D-50569 COLOGNE
Date: 15.10.2019