Durethan AKV30XTS2 901510

  _More Info 
  _Data sheet ISO (PDF) 

 

Data sheet

PA 66, 30% glass fibers, injection molding, high temperature stabilized, improved surface finish
 
ISO Shortname:  ISO 16396-PA 66,GF30,GHR,S14-100
PropertyTest ConditionUnitStandardguide value
 d.a.m.cond.
Rheological properties
CMolding shrinkage, parallel60x60x2%ISO 294-40.35
CMolding shrinkage, transverse60x60x2%ISO 294-40.7
Post- shrinkage, parallel60x60x2%ISO 294-40.1
Post- shrinkage, transverse60x60x2%ISO 294-40.18

Mechanical properties (23 °C/50 % r. h.)
CTensile modulus1 mm/minMPaISO 527-1,-2100006500
CTensile Stress at break5 mm/minMPaISO 527-1,-2190120
CTensile Strain at break5 mm/min%ISO 527-1,-237.5
CCharpy impact strength23 °CkJ/m²ISO 179-1eU6095
CCharpy impact strength-30 °CkJ/m²ISO 179-1eU5045
CCharpy notched impact strength23 °CkJ/m²ISO 179-1eA<1012
CCharpy notched impact strength-30 °CkJ/m²ISO 179-1eA<10<10
Izod impact strength23 °CkJ/m²ISO 180-1U5075
Izod impact strength-30 °CkJ/m²ISO 180-1U5050
Izod notched impact strength23 °CkJ/m²ISO 180-1A<1012
Flexural modulus2 mm/minMPaISO 178-A95006500
Flexural strength2 mm/minMPaISO 178-A280195
Flexural strain at flexural strength2 mm/min%ISO 178-A3.86.5
Flexural stress at 3.5 % strain2 mm/minMPaISO 178-A270160
CPuncture maximum force23 °CNISO 6603-2750920
CPuncture maximum force-30 °CNISO 6603-2700715
CPuncture energy23 °CJISO 6603-22.43.8
CPuncture energy-30 °CJISO 6603-22.22.1
Ball indentation hardnessN/mm²ISO 2039-1225

Thermal properties
CMelting temperature10 °C/min°CISO 11357-1,-3260
CTemperature of deflection under load1.80 MPa°CISO 75-1,-2235
CTemperature of deflection under load0.45 MPa°CISO 75-1,-2250
Vicat softening temperature50 N; 120 °C/h°CISO 306235
CCoefficient of linear thermal expansion, parallel23 to 55 °C10-4/KISO 11359-1,-20.23
CCoefficient of linear thermal expansion, transverse23 to 55 °C10-4/KISO 11359-1,-20.9

Electrical properties (23 °C/50 % r. h.)
CComparative tracking index CTISolution ARatingIEC 60112600

Other properties (23 °C)
CWater absorption (Saturation value)Water at 23 °C%ISO 626.3
CDensitykg/m³ISO 11831380

Processing conditions for test specimens
CInjection molding-Melt temperature°CISO 294290
CInjection molding-Mold temperature°CISO 29480

Processing recommendations
Drying temperature dry air dryer°C -80
Drying time dry air dryerh -2-6
Residual moisture content%Acc. to Karl Fischer 0.03-0.12
Melt temperature (Tmin - Tmax)°C -270-290
admissible residence time at Tmaxmin -<5
Mold temperature°C -80-100
CThese property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Disclaimer
Disclaimer for trial products
This is a trial product at the developmental stage. No definitive statements can therefore be made as to type conformity, processability, long-term performance characteristics or other production or application parameters. Therefore, the purchaser/user uses the trial product entirely at his own risk without having been given any warranty or guarantee and agrees that the supplier shall not be liable for any damage, of whatever nature, arising out of such use. Unless specified to the contrary, the values given have been established on standardized test specimens at room temperature. The figures should be regarded as non-binding approximate data only, and not as guide values or binding minimum values. Please note that, under certain conditions, the properties can be affected to a considerable extent by the design of the mold/die, the processing conditions and the coloring. The marketing and continued supply of this material are not assured and may be discontinued at any time. Our products are sold in accordance with the current version of our General Conditions of Sale and Delivery.
Processing note
Under the recommended processing conditions small quantities of decomposition product may be given off during processing. To preclude any risk to the health and well-being of the machine operatives, tolerance limits for the work environment must be ensured by the provision of efficient exhaust ventilation and fresh air at the workplace in accordance with the Safety Data Sheet. In order to prevent the partial decomposition of the polymer and the generation of volatile decomposition products, the prescribed processing temperatures should not be substantially exceeded. Since excessively high temperatures are generally the result of operator error or defects in the heating system, special care and controls are essential in these areas.
Conditioning
Conditioning in accordance with ISO 1110 (70 °C; 62 % r.h.)