Durethan BM40XH2.0 901510 DUS009

  _More Info 
  _Data sheet ISO (PDF) 

 

Data sheet

PA 6, 40 % glass fibers/mineral, injection molding, heat-aging stabilized
 
ISO Shortname:  ISO 16396-PA 6,(GF+MD)40,GHR,S14-080
PropertyTest ConditionUnitStandardguide value
 d.a.m.cond.
Rheological properties
CMolding shrinkage, parallel60x60x2; 290 °C / MT 80 °C; 600 bar%ISO 294-40.51
CMolding shrinkage, transverse60x60x2; 290 °C / MT 80 °C; 600 bar%ISO 294-40.67
Post- shrinkage, parallel60x60x2; 120 °C; 4 h%ISO 294-40.17
Post- shrinkage, transverse60x60x2; 120 °C; 4 h%ISO 294-40.15

Mechanical properties (23 °C/50 % r. h.)
CTensile modulus1 mm/minMPaISO 527-1,-280004000
CTensile Stress at break5 mm/minMPaISO 527-1,-211560
CTensile Strain at break5 mm/min%ISO 527-1,-22.6
CCharpy impact strength23 °CkJ/m²ISO 179-1eU4590
CCharpy impact strength-30 °CkJ/m²ISO 179-1eU4040
CCharpy notched impact strength23 °CkJ/m²ISO 179-1eA<10<10
CCharpy notched impact strength-30 °CkJ/m²ISO 179-1eA<10<10
Izod impact strength23 °CkJ/m²ISO 180-1U4070
Izod impact strength-30 °CkJ/m²ISO 180-1U3535
Izod notched impact strength23 °CkJ/m²ISO 180-1A<10<10
Izod notched impact strength-30 °CkJ/m²ISO 180-1A<10<10
Flexural modulus2 mm/minMPaISO 178-A8000
Flexural strength2 mm/minMPaISO 178-A190
Flexural strain at flexural strength2 mm/min%ISO 178-A3.4
CPuncture maximum force23 °CNISO 6603-2568
CPuncture maximum force-30 °CNISO 6603-2602
CPuncture energy23 °CJISO 6603-21.4
CPuncture energy-30 °CJISO 6603-21.5
Ball indentation hardnessN/mm²ISO 2039-1213

Thermal properties
CMelting temperature10 °C/min°CISO 11357-1,-3220
CTemperature of deflection under load1.80 MPa°CISO 75-1,-2191
CTemperature of deflection under load0.45 MPa°CISO 75-1,-2215
CTemperature of deflection under load8.00 MPa°CISO 75-1,-280
Vicat softening temperature50 N; 120 °C/h°CISO 306215
CCoefficient of linear thermal expansion, parallel23 to 55 °C10-4/KISO 11359-1,-20.35
CCoefficient of linear thermal expansion, transverse23 to 55 °C10-4/KISO 11359-1,-20.85
Burning behavior US-FMVSS302>=1.0 mm ISO 3795passed

Electrical properties (23 °C/50 % r. h.)
CComparative tracking index CTISolution ARatingIEC 60112425

Other properties (23 °C)
CWater absorption (Saturation value)Water at 23 °C%ISO 626
CWater absorption (Equilibrium value)23 °C; 50 % RH%ISO 621.8
CDensitykg/m³ISO 11831480
Bulk densitykg/m³ISO 60900

Processing conditions for test specimens
CInjection molding-Melt temperature°CISO 294290
CInjection molding-Mold temperature°CISO 29480

Processing recommendations
Drying temperature dry air dryer°C -80
Drying time dry air dryerh -2-6
Residual moisture content%Acc. to Karl Fischer 0.03-0.12
Melt temperature (Tmin - Tmax)°C -280-300
Mold temperature°C -80-120
CThese property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Disclaimer
Disclaimer for commercial products
This information and our technical advice - whether verbal, in writing or by way of trials - are given in good faith but without warranty, and this also applies where proprietary rights of third parties are involved. Our advice does not release you from the obligation to verify the information currently provided - especially that contained in our safety data and technical information sheets - and to test our products as to their suitability for the intended processes and uses. The application, use and processing of our products and the products manufactured by you on the basis of our technical advice are beyond our control and, therefore, entirely your own responsibility. Our products are sold in accordance with the current version of our General Conditions of Sale and Delivery.
Test values
Unless specified to the contrary, the values given have been established on standardized test specimens at room temperature. The figures should be regarded as guide values only and not as binding minimum values. Kindly note that, under certain conditions, the properties can be affected to a considerable extent by the design of the mould/die, the processing conditions and the coloring.
Processing note
Under the recommended processing conditions small quantities of decomposition product may be given off during processing. To preclude any risk to the health and well-being of the machine operatives, tolerance limits for the work environment must be ensured by the provision of efficient exhaust ventilation and fresh air at the workplace in accordance with the Safety Data Sheet. In order to prevent the partial decomposition of the polymer and the generation of volatile decomposition products, the prescribed processing temperatures should not be substantially exceeded. Since excessively high temperatures are generally the result of operator error or defects in the heating system, special care and controls are essential in these areas.
Conditioning
Conditioning in accordance with ISO 1110 (70 °C; 62 % r.h.)
LANXESS DEUTSCHLAND GMBH | D-50569 COLOGNE
Date: 01.05.2019